本文首先采用间歇法在一定温度、压力下,使用lewis酸为催化剂,合成了葡萄糖聚氧乙烯醚。并将此糖基聚氧乙烯醚表面活性剂应用到复合型泡沫混凝土发泡剂中,采用罗氏-迈尔斯（Ross-Miles）法测试其泡沫性能,通过罗氏泡沫仪的起泡高度和消泡半衰期,来研究发泡剂泡沫稳定性。实验结果表明,最佳复配条件为：以0.7%的十二烷基苯磺酸钠（LAS）,添加0.014%的聚丙烯酸树脂340作为基础起泡剂溶液,再加入0.014%的分子量为849的糖基聚氧乙烯醚表面活性剂,其起泡高度最高可达到167.5mm,且稳定性好,泡沫半衰期可达到56分钟。
Firstly, glucose ether was synthesized at a certain temperature and pressure, using the Lewis acid as the catalyst. Then sugar-based surfaetant was added to compound type of foaming agent, the effect on foaming agent was studied by measuring foaming height and defoaming half-life. An optimal formula was obtained as follows（wt%） ：0.7% sodium dodecyl benzene sulfonate （LAS）, 0. 014% carbomer 340, 0. 014% glucose ether with the molecular weight of 849. Using this formula, we can get the foaming height of 167.5mm, and the defoaming half-life of 56min.
参考文献
| [1] | 吴杰.建筑保温泡沫混凝土施工技术的研究与应用[J].绿色建筑,2010(03):60-62. |
| [2] | 李良.泡沫混凝土墙体和楼板研究[J].墙材革新与建筑节能,2010(09):18-21. |
| [3] | 袁俊,徐迅.泡沫混凝土的研究现状及发展动态[J].墙材革新与建筑节能,2007(04):31-33. |
| [4] | 曹雨新.浅析泡沫混凝土在国内外建筑工程中的应用[J].现代企业文化,2009(30):150-151. |
| [5] | 闫振甲;何艳君.泡沫混凝土实用生产技术[M].北京:化学工业出版社,2006:1-4. |
| [6] | 扈士凯,李应权,徐洛屹,段策,罗宁.国外泡沫混凝土工程应用进展[J].混凝土世界,2010(04):48-50. |
| [7] | 习志臻.混凝土泡沫剂的研究[J].江西建材,2000(03):5-8. |
| [8] | 高波,王群力,周孝德.混凝土发泡剂及泡沫稳定性的研究[J].粉煤灰综合利用,2004(01):13-16. |
| [9] | 王丽娟;张高勇;董金凤 等.泡沫性能的测试和评价方案进展[J].日用化学工业,2005,35(03):171-173. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%