采用乙烯基三乙氧基硅烷(VS)和正硅酸乙酯(TEOS)为原料,采用溶胶-凝胶法在AA5052铝合金表面制备了倍半硅氧烷(SSO)杂化膜.采用动电位极化法和电化学阻抗法测试了膜层的耐腐蚀性能,并考察了正硅酸乙酯的含量对其膜层的影响.结果表明,杂化膜能有效抑制AA5052铝合金的腐蚀反应,且当正硅酸乙酯的含量为20％时,杂化膜涂层的耐腐蚀性最好.
参考文献
| [1] | 王成,江峰,林海潮,余刚,丁晖.无机成膜型缓蚀剂对铝合金缓蚀作用的研究[J].腐蚀与防护,2000(12):539-541. |
| [2] | Joseph H.Osborne .Observations on chromate conversion coatings from a sol-gel perspective[J].Progress in Organic Coatings: An International Review Journal,2001(4):280-286. |
| [3] | R.L.Parkhill;E.T.Knobbe;M.S.Donley .Application and evaluation of environmentally compliant spray-coated ormosil films as corrosion resistant treatments for aluminum 2024-T3[J].Progress in Organic Coatings: An International Review Journal,2001(4):261-265. |
| [4] | Joseph H.Osborne;Kay Y.Blohowiak;S.Ray Taylor;Chad Hunter;Gordon Bierwagon;Brendon Carlson;Dan Bernard;Air force research laboratory nonmetallic mateirals directorate WPAFB OH 45433-7750 USA;Michael S. Donley .Testing and evaluation of nonchromated coating systems for aerospace applications[J].Progress in Organic Coatings: An International Review Journal,2001(4):217-225. |
| [5] | 尤宏,张兴文,吕祖舜,刘琰,张皓.正硅酸乙酯改性的GPMS有机-无机材料研究[J].材料科学与工艺,2003(04):430-433. |
| [6] | 潘建平.溶胶-凝胶法制备薄膜涂层的技术与应用[J].腐蚀与防护,2001(08):339-342. |
| [7] | 李传峰,邵怀启,钟顺和.有机无机杂化膜材料的制备技术[J].化学进展,2004(01):83-89. |
| [8] | 郭增昌,王云芳,王汝敏.铝合金表面不同硅烷化预处理的耐蚀性研究[J].中国腐蚀与防护学报,2007(03):172-175,180. |
| [9] | 尤宏,刘琰,孙德智,胡立江.LY12铝合金表面有机-无机杂化膜的防腐性能研究[J].材料工程,2004(06):7-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%