α+β钛合金微观组织对强韧性的影响概述

稀有金属材料与工程, 2012, 41(7): 1313-1316.

α+β钛合金微观组织对强韧性的影响概述

邵晖 ^1, , 赵永庆 ^2, , 曾卫东 ^3, , 葛鹏 ^4, , 杨义 ^5,

1.西北工业大学凝固技术国家重点实验室,陕西西安 710072;西北有色金属研究院,陕西西安 710016

2.西北有色金属研究院,陕西西安 710016

3.西北工业大学凝固技术国家重点实验室,陕西西安 710072

4.西北有色金属研究院,陕西西安 710016

5.西北有色金属研究院,陕西西安 710016

基金项目: 国家重点基础研究发展计划(973"计划)项目(2007CB613805)

关键词：强度 , 断裂韧性 , 组织 , α+β钛合金

Review on Influence of Microstructure on Strength and Fracture Toughness in α+β Titanium Alloy

α+β钛合金的微观组织对强度和断裂韧性有重要影响.本文概述了Ti-6Al-4V、Ti-62222s、Ti-6Al-2Sn-4Zr-6Mo等钛合金的拉伸性能、断裂韧性与组织特征参数的定性和定量关系.同时指出组织参数定量化、神经网络和有限元技术的综合利用可以有效预测组织和性能的关系.

参考文献

[1]	Yoshikuni Kawabe et al.[J].ISIJ International,1991,31(08):785.
[2]	Niinomi Mitsuo et al.[J].ISIJ International,1991,31(08):848.
[3]	Hirth J P et al.[J].Metallurgical and Materials Transactions,1977,8(07):1165.
[4]	Richards N L .[J].Journal of Materials Engineering and Performance,2004,13(02):218.
[5]	Beachem C D.Fractography-Microscopic Cracking Processes[M].Philadelphia,PA:ASTM International,1976:99.
[6]	Leyens C;et al;陈振华.钛与钛合金[M].北京:化学工业出版社,2005:140.
[7]	Hall J A et al.[J].Materials Science and Engineering,1972,9(04):197.
[8]	王F琦.[J].材料工程,2009(03):54.
[9]	Harold Margolin .[J].Metallurgical and Materials Transactions,1982,13(02):269.
[10]	Greenfield M A .[J].Metallurgical and Materials Transactions,1971,2(03):841.
[11]	Ltütjering G .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1998,243:32.
[12]	Niinomi M et al.[J].Materials Science and Technology,1988,4(09):803.
[13]	Hall I W;Hammond C .[J].Materials Science and Engineering,1978,32(03):241.
[14]	Campbell J E;et al;汪一麟.断裂力学在选材方面的应用[M].北京:冶金工业出版社,1992
[15]	朱知寿,王新南,童路,刘东升.新型TC21钛合金热处理工艺参数与显微组织演变的关系研究[J].钛工业进展,2006(06):24-27.
[16]	Terlinde G.[A].Marriott:Dever Co,1987:97.
[17]	Greenfield M A et al.[J].Metallurgical and Materials Transactions,1972,2(03):841.
[18]	Rogers D H.[A].New York:Plenum Press,1973:1719.
[19]	Lütjering G .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1999,263:117.
[20]	Wilson A W et al.[J].Metallurgical and Materials Transactions,1998,29:1585.
[21]	Niinomi M F et al.[J].Metallurgical and Materials Transactions,2001,32:2795.
[22]	Akmoulin I A et al.[J].Metallurgical and Materials Transactions,1994,25:1665.
[23]	Kuruvilia M et al.[J].Sadhana,2008,33(03):235.
[24]	Sauer C et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,31:393.
[25]	Lütjering G .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1996,213:71.
[26]	Peters J O et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1996,213(02):71.
[27]	Lütjering G .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,319:602.
[28]	张云琨,王树臣,郭劲.氢、氧对TC4机械性能和表面质量的影响[J].长春理工大学学报,2004(03):87-88.
[29]	张学敏,赵永庆,曾卫东.氢处理对TC21合金显微组织的影响[J].稀有金属材料与工程,2009(12):2179-2182.
[30]	Levin L.[A].Munich:Deutsche Gesellschaft für Metallkunde,1984:2107.
[31]	Bolisowa E A;陈石卿.钛合金金相学[M].北京:国防工业出版社,1986:243.
[32]	陈伟 .TC21钛合金损伤容限性的研究[D].南京:南京航空航天大学,2005.
[33]	张青 .热变形条件下TB8合金组织的分形及模拟[D].Hefei:Hefei University of Technology,2008.
[34]	王凯旋,曾卫东,赵永庆,邵一涛,周建华,王晓英,周义刚.钛合金片层α相在热加工过程中演变规律的定量研究[J].稀有金属材料与工程,2010(04):565-569.
[35]	任淮辉,李旭东,李俊琛.三维多晶体材料微结构的力学响应计算[J].兰州理工大学学报,2008(01):1-5.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

α+β钛合金微观组织对强韧性的影响概述

Review on Influence of Microstructure on Strength and Fracture Toughness in α+β Titanium Alloy

参考文献