The relationship between fracture toughness VGC and critical void growth RC/RO was studied for ten kinds of Steel. The macroscopic fracture toughness VGC was determined by using notched tensile specimens. and the microscopic parameters of critical void growth ratio RC/RO were quantitatively measured under SEM. Then, the coefhcient C in the relation VGC = C In(RC/RO) proposed in author's past work was specifically explored. The correlation of C with tensile proderty parameter φ=σyδ/(Eφn) was presented for the Steel investigated, and the effects of low temperature on C were also discussed. Results show that the coefficient C is linearly related to the parameter and insensitive to low temperature.