为改善羟基磷灰石（HA）/聚乳酸（PLA）复合材料降解后产生的局部酸性环境,提出Mg-HA/PLA复合材料的新体系,采用溶液共混法结合注塑工艺获得Mg-HA/PLA复合材料。采用扫描电镜、X射线衍射仪分析复合材料的显微相貌及物相组成,电子拉伸试验机测试复合材料的力学性能,模拟体液浸泡分析其降解特性。结果表明,采用溶液共混结合注塑工艺可以制备该复合材料;HA与Mg在PLA基体中未出现明显的团聚;HA、Mg与PLA三者保持各自物相;与5%（质量分数）HA/PLA复合材料相比,1.5%（质量分数）Mg添加对5%（质量分数）HA/PLA复合材料的力学性能影响不明显;Mg-HA/PLA复合材料浸泡4周后的pH值为7.41,而HA/PLA复合材料则为6.95。
In order to further neutralize the acidity during the degradation of HA（hydroxyapatite）/PLA（poly lactide acid） composites,a new type Mg-HA/PLA composites was proposed.The Mg-HA/PLA composites were prepared by using the solution blending method and combining injection molding process.The morphology and physical phase constitute of Mg-HA/PLA composites were analyzed by means of scanning electron microscopy（SEM） and X-ray diffraction（XRD）.The mechanical properties of composites materials were tested by electronic tensile testing machine,the simulated body fluid（SBF） was used to study the degradation behavior of Mg-HA/PLA composites.The results showed that Mg-HA/PLA composites were successfully fabricated by the solution blending method and combining the injection molding process,HA and Mg particles didn’t aggregated obviously in the PLA matrix and they maintained their phases respectively,the addition of 1.5wt% Mg had little effect on the mechanical properties of 5wt% HA/PLA composites,after 4th week,the pH value of solution of Mg-HA/PLA composites was 7.41,while the pH of the HA / PLA composites was 6.95.
参考文献
| [1] | 蒋毅,尹光福,周大利,张云,王玥华.羟基磷灰石/聚乳酸复合人工骨修复材料的研究进展[J].国外医学(生物医学工程分册),2004(04):238-241. |
| [2] | Taizo F;Yoshimura M;Tsunoru Y et al.Biodegradation behavior of ultra-high-strength hydroxyapatite/poly( Llactide)composite rods {or internal fixation of bone frac-tures[J].Biomaterials,2000,21:889-898. |
| [3] | McManus AJ;Doremus RH;Siegel RW;Bizios R .Evaluation of cytocompatibility and bending modulus of nanoceramic/polymer composites.[J].Journal of biomedical materials research, Part A,2005(1):98-106. |
| [4] | Hasegawa S;Neo M;Tamura J;Fujibayashi S;Takemoto M;Shikinami Y;Okazaki K;Nakamura T .In vivo evaluation of a porous hydroxyapatite/poly-DL-lactide composite for bone tissue engineering.[J].Journal of biomedical materials research, Part A,2007(4):930-938. |
| [5] | 蒋柳云,熊成东,李庆,白威,李玉宝.表面接枝处理的n-HA充填PLGA等温结晶行为的研究[J].功能材料,2011(09):1563-1568. |
| [6] | 肖素光,赵婧,翁杰.聚乳酸涂层改善网状羟基磷灰石陶瓷支架力学性能的研究[J].功能材料,2007(03):432-434. |
| [7] | Jaeobs J J;Gilbert J L;Urban R M .Corrosion of metal orthopedic implants[J].Journal of Bone and Joint Surgery,1998,80:268282. |
| [8] | Zreiqat H;Howlett C R;Zannettino A.Mecha nisms of magnesium-stimulated adhesion of osteoblastic cells to commonly used orthopedic implants[J].Biomedical Materials Research,2002:62,175-184. |
| [9] | Y. Yamasaki;Y. Yoshida;M. Okazaki .Synthesis of functionally graded MgCO_3 apatite accelerating osteoblast adhesion[J].Journal of biomedical materials research, Part B. Applied biomaterials,2002(1):99-105. |
| [10] | 任伊宾,黄晶晶,杨柯,张炳春,姚治铭,王浩.纯镁的生物腐蚀研究[J].金属学报,2005(11):1228-1232. |
| [11] | Schwach G;Vert M .[J].International Journal of Biological Macromolecules,1999,25:283-291. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%