为确定AZ31镁合金初始动态再结晶的临界条件或临界应变,通过在变形温度范围473～623 K、应变速率范围0.001～1 s-1条件下进行等温压缩试验,利用所得数据并采用单参数方法,建立起AZ31镁合金初始动态再结晶的临界条件,即临界应变(εc)与变形条件(引入温度补偿应变速率因子即Zener-Hollomon参数)的定量关系,并对不同应变下合金微观组织的演变规律进行了研究.
参考文献
| [1] | Galiyev A;Kaibyshev R;Gottstein G .[J].Acta Materialia,2001,49(07):1199. |
| [2] | Tan J C;Tan M J .[J].Materials Science and Engineering,2003,339(1-2):124. |
| [3] | Poliak E I;Jonas J J .[J].ISIJ International,2003,43(05):684. |
| [4] | Poliak E I;Jonas J J .[J].Acta Materialia,1996,44(01):127. |
| [5] | Na Y S;Rhyim Y M;Lee J H et al.[J].Materials Science Forum,2004,449-452(01):577. |
| [6] | Manonukul A;Dunne F P E .[J].Acta Materialia,1999,47(17):4339. |
| [7] | 马立强,袁向前,刘振宇,张丕军,焦四海,吴迪,王国栋.铌微合金钢动态再结晶的规律[J].钢铁研究学报,2006(09):47-50. |
| [8] | Verlinden B;Wouters P;McQueen H J et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1990,123(02):229. |
| [9] | Gourdet S;Montheillet F .[J].Acta Materialia,2003,51(09):2685. |
| [10] | Montheillet F .[J].Revue De Metallurgie,2002,99(09):767. |
| [11] | 张凯锋,尹德良,韩文波.热轧AZ31镁合金温变形中的微观组织演变[J].航空学报,2005(04):505-509. |
| [12] | Ryan N D;McQueen H J .[J].Canadian Metallurgical Quarterly,1990,29(02):147. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%