采用溶胶-凝胶方法,以正硅酸乙酯为先驱体,通过硝酸银引入银离子,在不锈钢表面制得银离子掺杂抗菌不锈钢薄膜.实验测试了薄模在10%FeCl3溶液的耐腐蚀性能,负载150 g和250 g的图钉刻划以及500 g绘图橡皮擦拭等机械性能.发现不锈钢表面氧化处理后,薄膜的耐腐蚀性能和机械性能都有很大的提高.通过XRD分析和抗菌性能测试证实SiO2在薄膜中是无定形状态,无法有效的固化银离子,样品的一次抗菌性能较好,长期浸泡后抗菌性能降低.
参考文献
| [1] | Keizer K;De Lange R S A;Hekkink J H A;Burggraaf A J .Polymeric-Silica-Based Sols for Membrane Modification Applications:Sol-Gel Synthesis and Characterization with SAXS[J].Journal of Non-Crystalline Solids,1995,191(01):1-16. |
| [2] | 张兆艳.影响SiO2薄膜中银粒子发光强度的因素分析[J].无机材料学报,2001(04):747-751. |
| [3] | Yoshio Onodera;Takashi Iwasaki;Abhijit Chatterjee .Bactericdal allophanic materials prepared form allophane soil I. Preparation and charactrization of silver/phosphorus-silver Loaded allophanic specimens[J].Applied clay science,2001(3/4):123-134. |
| [4] | Lin C J;Dub J G.Mechanical Characteristics of Colored Film on Stainless Steel by the Current Pulse Method[J].Thin Solid Films,1996(287):80-86. |
| [5] | 汪铭,丁新更,曹旭丹,杨辉.不锈钢基片上制备Ag+/TiO2抗菌薄膜的研究[J].材料科学与工程学报,2003(03):379-382. |
| [6] | 何宜柱;余亮;张吉人 .Research on the Phase Transformation Behavior during Crystallization of SiO2 Prepared by Sol-Gel Process[J].华东冶金学院学报,1993,10(04):27-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%