利用Gleeble-1500热模拟实验机对Fe-3%Si合金进行1173K、0.01s-1条件下的压缩变形,借助EBSD分析了不同应变量下晶界与热变形组织特征演变.发现晶体旋转动态再结晶机制与几何动态再结晶机制共同控制了动态再结晶过程:在小应变量阶段,晶体旋转的不均匀性使晶界附近区域优先形成完善亚晶,而晶粒内部呈现不完善的亚晶;随应变量增大,晶界附近区域取向差增加,小角晶界逐渐演变为大角晶界;在大应变量阶段,原始晶界附近区域形成的大角晶界相互接触,最终通过几何动态再结晶机制实现通体动态再结晶.
参考文献
| [1] | Davies R G .[J].Transactions TMS-AIME,1963,227:665-668. |
| [2] | Barrett C R .[J].Transactions TMS-AIME,1967,239:1726-1729. |
| [3] | Stang R G;Nix W D;Barrett C R .[J].Metallurgical and Materials Transactions,1973,4:1695-1699. |
| [4] | Uvira J L;Jonas J J .[J].Transactions TMS-AIME,1968,242:1619-1626. |
| [5] | Immarigeon J-P A;Jonas J J .[J].Acta Metallurgica,1974,22:1235-1247. |
| [6] | Inoue E;Sakai T .[J].Journal of the Japan Institute of Metals,1991,55:286-293. |
| [7] | S. Akta;G. J. Richardson;C. M. Sellarsa .Hot deformation and recrystallization of 3 percent silicon steel part 1: Microstructure, flow stress and recrystallization characteristics[J].ISIJ International,2005(11):1666-1675. |
| [8] | Gourdet S;Montheillet F .[J].Materials Science and Engineering,2000,A283:274-288. |
| [9] | McQueen H J;Blum W .[J].Materials Science and Engineering,2000,A290:95-107. |
| [10] | Eghbali B;Abdollah-Zadeh A;Beladi H et al.[J].Materials Science and Engineering,2006,A435-436:499-503. |
| [11] | Eghbali B;Abdollah-zadeh A;Hodgsonc P D .[J].Materials Science and Engineering,2007,A462:259-263. |
| [12] | Eghbali B .[J].Materials Characterization,2008,59:473-478. |
| [13] | Abdollah-Zadeh A;Eghbali B .[J].Materials Science and Engineering,2007,A457:219-225. |
| [14] | Humphreys F J;Hatherly M.Clinical and Investigative Medicine/Medicine Clinique at Experimentale[M].New York:Oxford,Pergamon Press,2005:451-467. |
| [15] | Drury M R;Humphreys F J .[J].Acta Metallurgica,1986,34(11):2259-2271. |
| [16] | Gholinia A;Humphreys F J;Prangnell P B .[J].Acta Materialia,2002,50:4461-4476. |
| [17] | Cabrera J M;Ponce J;Prado J M .[J].Journal of Materials Processing Technology,2003,143-144:403-409. |
| [18] | Yanagida A;Yanagimoto J .[J].Journal of Materials Processing Technology,2004,151:33-38. |
| [19] | Ion S E;Humphreys F J;White S .[J].Acta Metallurgica,1982,30(10):1909-1919. |
| [20] | Galiyev A;Kaibyshev R;Gottstein G .[J].Acta Materialia,2001,49:1199-1207. |
| [21] | Tan J K;Tan M J .[J].Materials Science and Engineering,2003,A339:124-132. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%