采用极化曲线和电化学阻抗法研究了H2S浓度、酸度以及液膜厚度对X70钢在含H2S薄层液膜下腐蚀行为的影响.结果表明,薄层液膜下,H2S促进了X70钢腐蚀的阴阳极过程;随着H2S浓度升高,自腐蚀电位(Ecorr)正移,自腐蚀电流密度(Jcorr)增大,腐蚀速率增加;pH减小,Ecorr负移,Jcorr增大;当pH＜3.02时,低频端—维扩散特征的Warburg阻抗由一感抗弧所代替;液膜厚度减薄,电荷传递电阻减小,X70钢腐蚀速率加快.
参考文献
| [1] | 王澎.H2S对天然气处理设备的腐蚀及相应对策[J].天然气与石油,2010(02):34-36. |
| [2] | 于英姿,米秋占,段贵华.输气管道的硫化物应力腐蚀分析[J].油气储运,2000(08):37-40. |
| [3] | Yameng Qi;Hongyun Luo;Shuqi Zheng;Changfeng Chen;Danni Wang .Effect of immersion time on the hydrogen content and tensile properties of A350LF2 steel exposed to hydrogen sulphide environments[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013(Apr.):164-174. |
| [4] | B.A. Lasebikan;A.R. Akisanya;W.F. Deans;D.E. Macphee .The effect of hydrogen sulphide on ammonium bisulphite when used as an oxygen scavenger in aqueous solutions[J].Corrosion Science,2011(12):4014-4025. |
| [5] | 郭红,何晓英,伍远辉.H2S对X70钢在弱酸性溶液中的腐蚀行为的影响[J].腐蚀科学与防护技术,2006(04):258-261. |
| [6] | 邓海英,何晓英,王红云,邓祖宇.X70钢在饱和CO2的HAc-NaAc溶液中的腐蚀行为[J].中国腐蚀与防护学报,2007(04):224-227. |
| [7] | 何晓英,邓祖宇,邓海英.（NH4）2SO4薄层液膜下X70钢腐蚀的电化学研究[J].腐蚀科学与防护技术,2008(03):213-215. |
| [8] | 李明,李晓刚,陈华.在湿H2S环境中金属腐蚀行为和机理研究概述[J].腐蚀科学与防护技术,2005(02):107-111. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%