研究了低合金高强度非调质中厚板钢中添加稀土(REM)和Ca、Mg微量元素对大线高能焊接热影响区(HAZ)显微组织微细化和晶内针状铁素体(IAF)形成的影响.结果表明,添加REM和Ca、Mg元素可在钢的HAZ中形成弥散稳定的氧硫化物(CeCa)2O2S和(CeMg)2O2,热轧奥氏体化(1450℃)和焊接热输入10 kJ/mm时都十分稳定,比传统采用TiN强化的钢具有更优良的低温韧性.有效地控制细小弥散的氧硫化合物,能获得适中的奥氏体有效晶粒尺寸和提供HAZ中形成晶内针状铁素体及稳定活性的形核位置.促进晶内铁素体协同形核生长,有效地使得HAZ组织微细化.
参考文献
| [1] | Aihara S;Shigesato G .Microstructural Control of Weld HeatAffected Zone of Steel by Mn Depletion Around Inclusions[J].Nippon Steel Technical Report,2004,381:39-44. |
| [2] | Kojma A;Hoshino M .Super High HAZ Toughness Technology With Fine Microstructure Imparted by Fine Particles[J].Nippon Steel Technical Report,2004,380:2-5. |
| [3] | Ricks R A;Howell P R .The Nature of Aeicular in HSLA Steel Weld[J].Journal of Meter Sci,1982,17(03):732. |
| [4] | Farrar R A;Harrison P L .Acicular Ferrite in Carbon-Manganese Weld Metals[J].Journal of Master Sci,1987,22:3812-3820. |
| [5] | Barbaro F J;Krauklis P .Easterling.Formation of Acicular Ferrite at Oxide Particles in Steels[J].Materials Science and Technology,1989,11(05):1057-1068. |
| [6] | J.-L. LEE;Y.-T. PAN .The formation of intragranular acicular ferrite in simulated heat-affected zone[J].ISIJ International,1995(8):1027-1033. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%