以Ti、Al、TiN粉为原料,采用热压烧结工艺在1400 ℃合成了含少量TiN和Al_3Ti的Ti_4AlN_3块体材料,分别研究了不同原料配比、烧结温度及合成时间下烧结试样的相组成.混合粉Ti/1.2Al/3TiN在1400 ℃下保温2 h所得烧结试样经背散射电子像结合EDS能谱分析,证实成功合成了Ti_4AlN_3材料.烧结试样晶粒尺寸为5～10 μm,晶体呈层状或板状结构,结晶良好,结构致密.相对密度达到99.3%,维氏硬度及电导率分别为3.9～5.1 GPa和1.2×10~6 Ω~(-1)·m~(-1),表明其具有优良的机械加工及导电性能.
Predominantly single-phase bulk samples of Ti_4AlN_3 with a few amounts of TiN and Al_3Ti was successfully synthesized by a hot-pressing method using Ti, Al and TiN powders as starting materials. The phase composition of the sintered samples with different starting composition, sintering temperature and holding time were presented. The results of BEI and EDS show that Ti_4AlN_3 is synthesized with the initial composition of Ti/1.2Al/3TiN at 1400 ℃ for 2 h.The sintered sample is fully dense and well-developed in laminate shape with dimension of 5-10 μm. The relative density of it reachs to 99.3%. Besides, the Vickers hardness and electrical conductivity are 3.4-4.5 GPa and 1.2×10~6 Ω~(-1)·m~(-1), which performs well on machinability and electrical property.
参考文献
| [1] | Michel W.Barsoum .The M_(N+1)AX_N Phases: A new Class of solids; Thermodynamically Stable Nanolaminates[J].Progress in Solid State Chemistry,2000(1/4):201-281. |
| [2] | Michel W. Barsoum;Tamer El-Raghy .The MAX Phases: Unique New Carbide and Nitride Materials[J].American Scientist,2001(4):334-343. |
| [3] | Zhou YC.;Sun ZM. .Electronic structure and bonding properties in layered ternary carbide Ti3SiC2[J].Journal of Physics. Condensed Matter,2000(28):L457-L462. |
| [4] | Barsoum M W;Brodkin D T;EI-Ranghy T .Layered machinable ceramics for high temperature application[J].Scripta Materialia,1997,36(05):535-541. |
| [5] | Rawn CJ.;El-Raghy T.;Procipio A.;Hoffmann CM.;Hubbard CR.;Barsoum MW. .Structure of Ti4AlN3 - a layered M(n+1)AX(n) nitride[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2000(11):1785-1796. |
| [6] | Y.S. Han;K.B. Kalmykov;S.F. Dunaev .Solid-State Phase Equilibria in the Titanium-Aluminum-Nitrogen System[J].Journal of Phase Equilibria and Diffusion,2004(5):427-436. |
| [7] | Zhou Y C;Sun Z M .Electronic structure and bonding properties of layered machinable Ti_2AlC and Ti_2AlN ceramics[J].Physical Review B,2000,61(19):12570-12573. |
| [8] | Zhimei Sun;Yanchun Zhou .Electronic Structure and Structural Properties of Ti_4AlN_3 Investigated by Ab initio Calculations[J].Journal of the Physical Society of Japan,2002(5):1313-1317. |
| [9] | Michel W. Barsoum;Dmitri Brodkin;Tamer El-Raghy .Layered machinable ceramics for high temperature applications[J].Scripta materialia,1997(5):535-541. |
| [10] | Barsoum M W;Ali M .Processing and characterization of Ti_2AlC,Ti_2AlN and Ti_2AlC_(0.5)N_(0 5)[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31(07):1857-1865. |
| [11] | Yan M;Chen Y L;Mei B C et al.Synthesis of high-purity Ti_2AlN ceramics by hot pressing[J].Transactions of Nonferrous Metals Society of China,2008,18:82-85. |
| [12] | Lin Z J;Zhou M J;Li M S.Synthesis and microstructure of layered-ternary Ti_2AlN ceramics[J].Scripta Materialia,2007(56):1115-1118. |
| [13] | A.T.Procopio;T.E.Raghy .Synthesis of Ti_4AlN_3 and phase equilibria in the Ti- Al-N system[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(2):373-378. |
| [14] | Ohnuma I.;Fdujita Y. .PHASE EQUILIBRIA IN THE Ti-Al BINARY SYSTEM[J].Acta materialia,2000(12):3113-3123. |
| [15] | A.T.Procopio;T.E.Raghy .Characterization of Ti_4AlN_3[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(2):333-337. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%