研究了热处理后TiN涂层在模拟海水中的腐蚀行为,采用电化学阻抗谱（EIS）、动电位极化曲线、扫描电镜和能谱分析等技术研究了热处理后TiN涂层电化学腐蚀参数及组织的变化。结果表明：热处理后TiN涂层的耐蚀性明显提高,自腐蚀电流仅为热处理前的13.3%,极化电阻约是热处理前的20倍;电化学阻抗谱描绘了热处理后涂层的腐蚀过程及导致涂层腐蚀的主要因素,涂层局部的孔隙腐蚀是引起电化学腐蚀参数变化的主要因素,腐蚀初期孔隙电阻由大变小,后期又会由小变大,从而使涂层的腐蚀速率发生变化;热处理会使涂层的通孔率降低为87%,主要原因是在热处理过程,TiN与大气中的O2发生了氧化反应,生成密度较TiN小的TiO2相和Ti3O相,使涂层中的部分通孔被封闭,耐蚀性得以提高。
Corrosion behavior of TiN coatings after heat treatment in simulated seawater was studied.The change of the electrochemical corrosion parameters and the structure of TiN coating after heat treatment were investigated by electrochemical impedance spectroscopy（EIS）,potentiodynamic polarization curve,SEM and EDS analysis.The results show that the corrosion resistance of the coatings after heat treatment is increased,and its corrosion current is only 13.3% of the untreated coatings,and the polarization resistance of the heat treated TiN coatings is 20 times of that of the untreated coatings;EIS results show the corrosion process of the heat treated TiN coatings and the factors leading to the corrosion of the coatings.The local corrosion at pores in the coatings is the main factor which makes the changes of electrochemical corrosion parameters,and the pore resistance decreases in initial immersion stage and increases in late stage,which leads to the variation of corrosion rate of the TiN coatings;after heat treatment,the through porosity in the coatings decreases to 87% of the untreated coatings.It is found that during the heat treatment TiN coatings reacts with oxygen to form TiO2 and Ti3O which have lower density than TiN,therefore the partial through pores are blocked and the corrosion resistance of the TiN coatings increases.
参考文献
| [1] | 曾霞文,谭彦显,陈超,杨晓红,蔡素玲.纳米TiN涂层改性技术在塑料模具中的研究与应用[J].机电工程技术,2009(10):94-96. |
| [2] | 林香祝,张敏,徐世珍.气相沉积技术在模具上的应用[J].西安理工大学学报,2001(04):408-412. |
| [3] | Hal K;Sawase T;M atsumura H et al.Corrosion resistance of a magnetic stainless steel ion-plated with titanium nitride[J].Journal of Oral Rehabilitation,2000,27(04):561-366. |
| [4] | 陈洁,胡滨.TiN涂层对牙科钴铬合金耐蚀性能的影响[J].上海交通大学学报（医学版）,2009(06):660-662,676. |
| [5] | Beverskog B;Carlsson J O;Delblanc Bauer A et al.Corrosion properties of TiC fi|m prepared by active reactive evaporation[J].Surface and Coatings Technology,1990,41:221. |
| [6] | Rudenja S;Pan J;Odnevall Wallinder I et al.Passivation and anodic oxidation of duplux TiN coating on stainless steel[J].Journal of the Electrochemical Society,1999,146:4082. |
| [7] | Morimoto J;Sasaki Y;Fukuhara S;Abe N;Tukamoto M .Surface modification of Cr3C2-NiCr cermet coatings by direct diode laser[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2006(11/12):1400-1405. |
| [8] | Utu D;Brandl W;Marginean G et al.Morphology and phase modification of HVOF-sprayed MCrAIY-coatings remeletd by electron beam irradiation[J].Vacuum,2005,77(04):451-455. |
| [9] | Cheng Z.;Xie GW.;Shi YL.;Peng HR. .Annealing studies of TiN films deposited by plasma-assisted CVD[J].Surface & Coatings Technology,2001(2/3):237-241. |
| [10] | Chou WJ.;Yu GP.;Huang JH. .Effect of heat treatment on the structure and properties of ion-plated TiN films[J].Surface & Coatings Technology,2003(1):43-50. |
| [11] | E. Arslan;I Efeoglu .Effect of heat treatment on TiN films deposited by CFUBMS[J].Materials Characterization,2004(1):29-34. |
| [12] | Huang JH;Yu KJ;Sit P;Yu GP .Heat treatment of nanocrystalline TiN films deposited by unbalanced magnetron sputtering[J].Surface & Coatings Technology,2006(14/15):4291-4299. |
| [13] | Xi Yingxue;Fan Huiqing;Liu Weiguo .The effect of annealing treatment on microstrueture and properties of TiN films prepared by unbalanced magnetron sputtering[J].Journal of Alloys and Compounds,2010,496(1 -2):695-698. |
| [14] | 陆晨光,阎殿然,董艳春,李凌云,赵春晓.反应等离子喷涂TiN涂层热处理后力学性能研究[J].稀有金属材料与工程,2009(z1):129-132. |
| [15] | Hsu Cheng-hsun;Chen Ming-li;Lai Kuei-laing .Corrosion resistance of TiN/TiAIN-coated ADI by cathodic arc deposition[J].Materials Science and Engineering A,2006,421(1 - 2):182-190. |
| [16] | Urgen M;Cakir AF .The effect of heating on corrosion behavior of TiN- and CrN-coated steels[J].Surface & Coatings Technology,1997(2/3):236-244. |
| [17] | Galvanetto E;Borgioli F;Galliano FP;Bacci T .Improvement of wear and corrosion resistance of RPS Ti-TiN coatings by means of thermal oxidation[J].Surface & Coatings Technology,2006(11):3650-3655. |
| [18] | 佟树善;傅正生 .陶瓷涂层穿透孔隙率的电化学测量[J].武汉水运工程学院学报,1991,15(01):75-81. |
| [19] | 董艳春 .反应等离子喷涂纳米TiN涂层材料的研究[D].河北工业大学,2006. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%