Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron

钢铁研究学报(英文版), 2013, 20(10): 81-86.

^1, , ^2, , ^3, , ^4, , ^5,

1.School of Materials Engineering, Yancheng Institute of Technology, Yancheng 224051, Jiangsu, China

2.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

3.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

4.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

5.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

基金项目: Natural Science Foundation of Jiangsu Province of China(BK2012250) Research Fund of Key Laboratory for Advanced Technology in Environmental Protection of Jiangsu Province of China(AE201035) Item Sponsored by National Natural Science Foundation of China(51071078)

Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron

YANG Zi-run ^1, , LI Dong-sheng ^2, , WANG Lan ^3, , WANG Shu-qi ^4, , WEI Min-xian ^5,

1.School of Materials Engineering, Yancheng Institute of Technology, Yancheng 224051, Jiangsu, China

2.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

3.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

4.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

5.School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

Keywords： spheroidal graphite cast iron

参考文献

[1]	A. De Santis;O. Di Bartolomeo;D. Iacouiello;F. Iacoviello .Quantitative shape evaluation of graphite particles in ductile iron[J].Journal of Materials Processing Technology,2008(1-3):292-302.
[2]	Quinn T F J;Sullivan J L;Rowson D M .Developments in the Oxidational Theory of Mild Wear[J].Tribology International,1980,13(04):153.
[3]	Wilson J E;Stott F H;Wood G C .The Development of Wear Protective Oxides and Their Influence on Sliding Friction[J].Proceedings of the Royal Society,1980,369A:557.
[4]	Inman I A;Datta S;Du H L et al.Microscopy of Glazed Layers Formed During High Temperature Sliding Wear at 750 ℃[J].Wear,2003,254(5/6):461.
[5]	Straffelini G.;Molinari A.;Trabucco D. .Oxidative wear of heat-treated steels[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):485-491.
[6]	O. Barrau;C. Boher;R. Gras;F. Rezai-Aria .Analysis of the friction and wear behaviour of hot work tool steel for forging[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(7/12):1444-1454.
[7]	Garza Montes-de-Oca N F;Rainforth W M .Wear Mechanisms Experienced by a Work Roll Grade High Speed under Different Environmental Condition[J].Wear,2009,267(1-4):441.
[8]	S. Q. Wang;M. X. Wei;F. Wang;Y. T. Zhao .Transition of elevated-temperature wear mechanisms and the oxidative delamination wear in hot-working die steels[J].Tribology International,2010(3):577-584.
[9]	S. Q. Wang;M. X. Wei;Y. T. Zhao .Effects of the tribo-oxide and matrix on dry sliding wear characteristics and mechanisms of a cast steel[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2010(5/6):424-434.
[10]	M. X. Wei;K. M. Chen;S. Q. Wang;X. H. Cui .Analysis for Wear Behaviors of Oxidative Wear[J].Tribology letters,2011(1):1-7.
[11]	A. R. Riahi;A. T. Alpas .Wear map for grey cast iron[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/6):401-409.
[12]	Y.C. Liu;J.M. Schissler;T.G. Mathia .The influence of surface oxidation on the wear resistance of cast iron[J].Tribology International,1995(7):433-438.
[13]	K. Hirasata;K. Hayashi;Y. Inamoto .Friction and wear of several kinds of cast irons under severe sliding conditions[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(1/6):790-800.
[14]	Prasad B K .Sliding Wear Reponse of Cast Iron as Influenced by Microstructural Features and Test Condition[J].Materials Science and Engineering,2007,456A(1/2):373.

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%