亚包晶钢连铸过程中常出现表面纵裂质量问题,与其在结晶器内较大高温相变收缩引起的初生坯壳不均匀生长密切相关,其纵裂纹敏感性可由包晶特征点计算出的包晶转变率判定.利用Factsage热力学计算软件研究钢种常见合金元素对Fe-C二元平衡相图中包晶特征点的影响,回归得到包晶特征点的预测公式.基于预测公式,可准确判断一定成分钢种的亚包晶范围,从而指导实际连铸生产中保护渣的选择.研究表明,通过合理的成分微调可有效降低包晶转变率,降低亚包晶钢高温相变收缩程度,甚至改变凝固模式变为过包晶模式,从而大大降低连铸坯纵裂纹敏感性.
参考文献
| [1] | Martin Herrera Trejo;Eddy Alfaro Lopez;Jose Jorge Ruiz Mondragon .Effect of Solidification Path and Contraction on the Cracking Susceptibility of Carbon Peritectic Steels[J].Metals and Materials International,2010(5):731-737. |
| [2] | Matsuura K;Kudoh M .Peritectic Transformation During Cooling of Iron-carbon Alloy[J].Metals and Materials,1998,4(03):562. |
| [3] | Hideo MIZUKAMI;Akihiro YAMANAKA;Tadao WATANABE .High Temperature Deformation Behavior of Peritectic Carbon Steel during Solidification[J].ISIJ International,2002(9):964-973. |
| [4] | Guyot V;Martin J;Ruelle A et al.Control of Surface Quality of 0.08％-0.12％ Steel Slabs in Continuous Casting[J].ISIJ International,1996,36(Supplement):223. |
| [5] | 蔡开科;程士富.连续铸钢原理与工艺[M].北京:冶金工业出版社,2007 |
| [6] | Wolf M M.Continuous Casting:Initial Solidification and Strand Surface Quality of Peritectic Steels[M].USA:Iron and Steel Society,1997 |
| [7] | Grill A;Brimacombe J K.Influence of Carbon Content on Rate of Heat Extraction in the Mould of a Continuous Casting Machine[J].Ironmaking and Steelmaking,1976(02):76. |
| [8] | Kagawa A;Okamoto T .Influence of Alloying Elements on Temperature and Composition for Peritectic Reaction in Plain Carbon Steels[J].Materials Science and Technology,1986,2(10):998. |
| [9] | Blazek K E;Lanzi O;Cano P L.Calculation of the Peritectic Range for Steel Alloys[J].Iron and Steel Technology,2008(06):80. |
| [10] | Robert Shepherd;Ingo Knopp;Heinz-GGnter Brass .Improved Determination of the Effect of Alloying Elements on the Peritectic Range in Low-Alloyed Cast Steel[J].Iron & Steel Technology,2012(10):77-85. |
| [11] | Xu J;He S;Wu T et al.Effect of Elements on Peritectic Reaction in Molten Steel Based on Thermodynamic Analysis[J].ISIJ International,2012,52(10):1856. |
| [12] | 苏留记;王泽民;黄华 .连铸圆管坯热裂纹与包晶点的关系[J].钢管,1998,27(01):12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%