以焦宝石铝酸钙水泥等为主要原料，研究了不同SiO2微粉加入量对焦宝石基喷涂耐火材料经自然干燥24h脱模后，再经110℃烘干24h，在不同温度煅烧3h后的体积密度以及热膨胀系数和抗热震性能的影响，并用扫描电镜观察了试样的显微组织。结果表明：焦宝石基喷涂耐火材料随着SiO2微粉含量的增加，体积密度增大，热膨胀系数减小；SiO2微粉质量分数为5％时，焦宝石基喷涂耐火材料具有最佳的抗热震性能。
The effects of different silica micropowders addition on the volume density, thermal expansion coefficient and thermal shock resistance properties of flint clay based spraying refractory were studied by taking flint clay, aluminate cement and so on as main raw material. Mold unloading after natural drying for 24 h and drying at 110℃ for 24 h, the specimens were calcined at different temperatures for 3 h, respectively. The microstructure was observed by SEM. The results show that volume density of flint clay based spraying refractory increased and thermal expansion coefficient decreased with the increase of silica micropowders additiora The flint clay based spraying refractory performed the best thermal shock resistance when the content of silica micropowders was 5wt%.
参考文献
| [1] | 张巍,戴文勇.氧化铝微粉在轻质隔热浇注料中的应用研究[J].陶瓷,2010(02):23-25. |
| [2] | 张巍,戴文勇.板状刚玉细粉和氧化铝微粉对铝矾土基喷涂料性能的影响[J].耐火材料,2010(03):221-222. |
| [3] | 张巍,吴洋,戴文勇,小宫山勇.热处理温度对焦宝石基喷涂料性能的影响[J].耐火与石灰,2009(01):20-21,24. |
| [4] | ZHANG Wei,DAI Wenyong.Effect of Boric Acid on Properties of Calcined Flint Clay-Bauxite Castables[J].中国耐火材料（英文版）,2010(03):24-27. |
| [5] | 张巍,李亮,戴文勇.焦宝石基喷涂料的研制[J].耐火材料,2009(06):458-459. |
| [6] | 张巍,戴文勇,千代田修明.堇青石对莫来石-铝矾土浇注料性能的影响[J].硅酸盐通报,2009(06):1286-1290. |
| [7] | 张巍,韩亚苓,吴嘉希,吴旭.氧化铝-锂霞石复合陶瓷在钢水中抗热震性研究[J].硅酸盐通报,2008(02):242-246,253. |
| [8] | Zhang Wei,韩亚苓.氧化铝基陶瓷抗热震性的研究进展[J].陶瓷学报,2008(02):193-198. |
| [9] | ZHANG Wei,DAI Wenyong,YU Xinfeng,LI Liang.Effect of Heat Treatment Temperature on Properties of Chinese Calcined Flint Clay Based Plastic Refractories[J].中国耐火材料（英文版）,2009(02):27-29. |
| [10] | 张巍,李雪东,戴文勇.不同酸碱性SiO2微粉在铝硅系不定形耐火材料中的应用[J].世界钢铁,2010(06):67-70. |
| [11] | 张巍,戴文勇.不同粒度叶腊石对铝矾土基喷涂料性能的影响[J].矿物学报,2010(02):230-234. |
| [12] | 张巍,李雪东,戴文勇.SiO2微粉含量对铝硅系耐火材料组织与性能的影响[J].金属热处理,2011(01):72-75. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%