高密度聚乙烯纤维表面活化及其与环氧复合材料的界面

材料研究学报, 1996, 10(6): 669-672.

高密度聚乙烯纤维表面活化及其与环氧复合材料的界面

山东建筑材料工业学院

关键词：聚乙烯纤维 , ( Department of Applied Chemistry , Shandong institute of Building Materials

SURFACE ACTIVATION OF HDPE FIBER AND THE INTERFACE OF PE FIBRE / EPOXY RESIN COMPOSITE

ZHOU Chunhua , LIU Wei , LI Xuemin , FAN Min(Shandong Institute of Building Materials)

Keywords： : PE fibre epoxy resin interface of compositeCorrespondent: ZHOU Chunhua , 环氧树脂 , 复合材料界面

采用铬酸氧化法处理聚乙烯纤维(HDPE)表面,并用SEM和XPS观察.结果表明,纤维表面活性提高,HDPE纤维/环氧树脂基复合材料界面粘接状况得以改善.界面粘接性能改善的主要原因可能是表面处理引入的多种含氧基团与环氧树脂分子中的环氧基团形成化学键力.

In this paper, the surfaces of HDPE fibre treated by chromic acid was investigated by meansof SEM and XPS. The results showed that the surface reactivity of acid-treated PE fibre changedsignificantly. Interfacial adhesion of PE fibre-reinforced epoxy resi

参考文献

[1]

LadizeslyNK,WardIM．JournalofMaterialsScience,1983,18(2):5332NardinM,WardIM．MaterialsScienceandTechnology,1987,3(10):8143袁超廷,高尚林等．复合材料新进展学术会议论文集,北京:中国复合材料学会,1991:1284张晔．复合材料新进展学术会议论文集,北京:中国复合材料学会,1991:1575笪有仙．复合材料学报,1994,11(4):146杨桂生,卢风才等．高分子学报,1992,6:7087HullD著,张双寅,郑维平等译．复合材料导论,北京:中国建筑工业出版社,1989:578宋焕成,赵时熙等．聚合物基复合材料,北京:国防工业出版社,1986:247"

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
周春华刘威李学闵范敏
在百度学术搜索
周春华刘威李学闵范敏
在万方数据库搜索
周春华刘威李学闵范敏
在CNKI搜索
周春华刘威李学闵范敏

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网