The Ti-48Al alloy was pack siliconized with 15%Si+85%Al2 O3. The microstructure of the siliconized coating on the TiAl-based alloy was analyzed and its effect on oxidation resistance was investigated. The specimens before and after cycle oxidation were examined by XRD and SEM equipped with XEDS. The results showed that the coating is composed of a thin Al2 O3 outer layer and a composite inner layer of Ti5Si3 with an appropriate amount of Al2 O3 dispersed in. Cycle oxidation tests showed that the high temperature oxidation resistance of TiAl-based alloy was greatly improved by forming such composite coating. No spallation and crack happened and the weight gain was very small after cycle oxidation at 900℃ for 314h.
参考文献
| [1] | S Taniguchi .[J].Materials and Corrosion,1997(48):1. |
| [2] | G Meier.[J].Materials and Corrosion,1996:595. |
| [3] | A. Rahmel;W. Quadakkers;M. Schutze.[J].Materials and Corrosion,1995:271. |
| [4] | K. Chan;Y.W. Kim.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993:113. |
| [5] | H.L. Qu;L. Zhou;H.R. Wei;Y.Q. Zhao.[J].Materials Review,2000:32. |
| [6] | Y Shida;H Anada .[J].Oxidation of Metals,1996(45):197. |
| [7] | S Taniguchi;T Shibata;A Murakami .[J].Oxidation of Metals,1994(41):103. |
| [8] | M Yoshihara;T Suzuki;R Tanaka .[J].ISIJ International,1991(31):1201. |
| [9] | S C Kung .[J].Oxidation of Metals,1990(34):217. |
| [10] | D Xu;Z H Zheng;X H Liu;S.C. Zou, S. Taniquchi, T. Shibata and T. Yamada .[J].Surface and Coatings Technology,1994(66):486. |
| [11] | S Taniguchi;T Shibata;N Asanuma;H.Lou,F.Wang and W.Wu .[J].Oxidation of Metals,1993(39):457. |
| [12] | S Taniguchi;T Shibata;K Takeuchi .[J].MATERIALS TRANSACTIONS,1991(32):299. |
| [13] | S C Huang .[J].Metallurgical and Materials Transactions,1991,A22:427. |
| [14] | S C Huang .[J].Metallurgical and Materials Transactions,1991,A22:2619. |
| [15] | K Hashimoto;H Doi;K Kasahara .[J].Journal of the Japan Institute of Metals,1988(52):1159. |
| [16] | Z G Liu;G Frommeyer;M Kreuss .[J].Scripta Metallurgica et Materialia,1991(25):120. |
| [17] | H E Devee;A G Evans;G R Odette;R.Mehrabian,M.L.Emiliani and R.J.Hecht .[J].Acta Materialia,1990(38):1491. |
| [18] | S. Taniguchi;T. Kuwayama;Y. -C. Zhu;Y. Matsumoto;T. Shibata .Influence of silicon ion implantation and post-implantation annealing on the oxidation behaviour of TiAl under thermal cycle conditions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):229-236. |
| [19] | U. Hornauer;R. Gunzel;H. Reuther;E. Richter;E. Wieser;W. Moller;G. Schumacher;F. Dettenwanger;M. Schutze .Protection of γ-based TiAl against high temperature oxidation using ion implantation of chlorine[J].Surface & Coatings Technology,2000(1/3):89-93. |
| [20] | H.N.Lee;Z.M.Park .Oxidation behaivor and mechanical properties of yttrium-doped L1_2(Al, Cr)_3 Ti coating on TiAl alloys[J].Scripta materialia,1999(10):1073-1078. |
| [21] | Z.L. Tang;F.H. Wang;W.T. Wu.[J].Materials Science and Engineering A,2000:70. |
| [22] | W.Liang;X.G.Zhao .IMPROVING THE OXIDATION RESISTANCE OF TiAl-BASED ALLOY BY SILICONIZING[J].Scripta materialia,2001(7):1049-1054. |
| [23] | C.G. Zhou;H.B. Xu;S.K. Gong.[J].Materials Science and Engineering A,2003:169. |
| [24] | H G Jung;D J Jung;K Y Kim .[J].Surface and Coatings Technology,2002(154):75. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%