Corrosion behavior of heavily drawn bundled Copper-niobium filamentary micro-composite was studied as a function of niobium content to develop the relationshipbetween microstructure and corrosion behavior in aqueous 30% HCl-FeCl3 solution.TEM observation revealed that niobium filaments were distributed regularly in coppermatrix along the sides of a triangular unit cell in the transverse section and more sub-grain boundaries were absorbed at copper/niobium phase boundaries with increasingniobium content. The corrosion potential and rate in aqueous 30% HCl-10% FeCl3 was-680.3mVSHE and 1.179×10-5A/cra2. The corrosion potential and rate decreasedas increasingniobium content and FeCl3. The yield stress can be described as thesum of the substructure strengthening component due to elongated grains, subgrainsand/or cells, the phase boundary strengthening term associated with the Hall-Petchtype interaction between dislocations and phase boundaries and precipitate strength-ening component.
参考文献
| [1] | J Bevk;J P Harbison;J L Bell .[J].Journal of Applied Physics,1978(49):6031. |
| [2] | W A Spitzing;P D Krotz .[J].Screen,1987(21):1143. |
| [3] | C L Tryus;L S Chumbley;W A Spitzig;J D Verhoeven .[J].ULTRAMICROSCOPY,1989,22:315. |
| [4] | P D Funkenbush;T H Courtney .[J].Screen,1990(24):1175. |
| [5] | W A Spitzing;F C Laabs;H L Downing;C V Renud .[J].Materials and Manufacturing Processes,1992,7(07):1. |
| [6] | S I Hong;M A Hill;Y Sakai;T J Wood J D Embury .[J].Acta Metallurgica Et Materialia,1995(43):313. |
| [7] | M Purrbaix .Atlas of Electrochemical Equilibria in Aqueous Solution[Z].National Association of Corrosion Engineers,Houghton,TX USA,1974. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%