针对国内核电站再热双阀组阀杆表面乙炔气堆焊CoCrW制备耐磨焊层无法满足60年服役寿命要求的问题,在阀杆材料(304不锈钢)表面激光熔覆Ni60/石墨/MoS2复合涂层.采用X射线衍射(XRD)、扫描电镜(SEM)和显微硬度检测等技术研究了熔覆层组织结构、相组成、显微硬度.结果表明,试样C2熔覆层从底部到顶部,熔覆层晶体依次为:平面晶、胞状晶、胞-树枝状晶、柱状树枝晶、等轴树枝晶,且平均硬度最高,为990 HV0.3.随着激光功率的升高,各类熔覆层硬度的波动幅度逐渐减小,硬质相的分布也随之越来越均匀.
参考文献
| [1] | 蔡振兵,朱旻昊,刘军,徐轶,俞佳,周仲荣.激光熔覆Ni60和Co-Cr-W合金层的高温磨损特性研究[J].润滑与密封,2006(04):26-28,31. |
| [2] | 刘双 .核阀密封面无钴镍基合金涂层材料及熔覆工艺研究[D].苏州大学,2010. |
| [3] | 魏宏璞 .核阀密封面无钴铁基合金及激光涂层性能研究[D].苏州大学,2010. |
| [4] | T. Baldridge;G. Poling;E. Foroozmehr;R. Kovacevic;T. Metz;V. Kadekar;M.C. Gupta .Laser cladding of Inconel 690 on Inconel 600 superalloy for corrosion protection in nuclear applications[J].Optics and Lasers in Engineering,2013(2):180-184. |
| [5] | Han Won-Jin;Kim Woo-Sung;Lee Seon-Ho.Development of laser cladding repair system for damaged alloy 600 heat exchanger tubes[A].Orlando:Laser Institute of America,2006:522. |
| [6] | Geyan Fu;Shuang Liu;Jiwei Fan .The design of cobalt-free, nickel-based alloy powder (Ni-3) used for sealing surfaces of nuclear power valves and its structure of laser cladding coating[J].Nuclear engineering and design,2011(5):1403-1406. |
| [7] | 杨胶溪,刘发兰,缪宣和,王志成.激光熔覆TC4/Ni/MoS2自润滑涂层的组织与摩擦学特性[J].金属热处理,2011(08):93-96. |
| [8] | 6061铝合金表面激光熔覆稀土CeO2+Ni60组织及耐蚀性[J].材料热处理学报,2014(06):148-152. |
| [9] | 张群莉,徐卫仙,姚建华,陈赵扬,马淳安.Co/介孔WC激光复合涂层的显微结构与高温磨损性能研究[J].中国激光,2014(05):73-78. |
| [10] | 余廷,邓琦林,张伟,董刚,杨建国.激光熔覆NiCrBSi合金涂层的裂纹形成机理[J].上海交通大学学报,2012(07):1043-1048. |
| [11] | 钛合金TC4激光熔覆NiCrBSi+Ni/MoS2涂层组织和摩擦磨损性能[J].材料热处理学报,2014(06):157-162. |
| [12] | 高强.最新有色金属金相图谱大全[M].北京:冶金工业出版社,2005 |
| [13] | 朱润生.Ni60自熔合金粉末的研究[J].粉末冶金工业,2002(06):7-16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%