用环氧树脂E12为基体,配合酚类固化剂及其他助剂,经熔融共混制备出低温固化环氧粉末涂料.考察了固化剂、促进剂用量等对体系固化性能、附着力及耐冲击性的影响,并通过非等温差示扫描量热法及红外光谱研究了酚羟基/环氧体系的固化反应.实验结果表明:随着固化剂用量增加,涂膜耐冲击性能先提高后减小;随着促进剂用量的增加,体系固化温度降低,附着力和耐冲击性提高.固化剂、促进剂最佳用量分别为环氧树脂E-12用量的20％和2.0％.
参考文献
| [1] | SALLA J M;MORANCHO J M;CADENATO A et al.Non-isothermal degradation of a thermoset powder coating in inert and oxidant atmospheres[J].Journal of Thermal Analysis and Calorimetry,2003,72(02):719-728. |
| [2] | Mafi R;Mirabedini SM;Attar MM;Moradian S .Cure characterization of epoxy and polyester clear powder coatings using Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA)[J].Progress in Organic Coatings: An International Review Journal,2005(3):164-169. |
| [3] | Maurin, V.;Croutxé-Barghorn, C.;Allonas, X. .Photopolymerization process of UV powders. Characterization of coating properties[J].Progress in Organic Coatings: An International Review Journal,2012(2/3):250-256. |
| [4] | Wuzella, G.;Kandelbauer, A.;Mahendran, A.R.;Teischinger, A. .Thermochemical and isoconversional kinetic analysis of a polyester-epoxy hybrid powder coating resin for wood based panel finishing[J].Progress in Organic Coatings: An International Review Journal,2011(4):186-191. |
| [5] | 孙国良,刘治猛,刘煜平,钟赤锋,贾德民.环氧粉末涂料低温固化剂的合成及应用[J].应用化工,2008(12):1432-1435,1439. |
| [6] | Merfeld G;Molaison C;Koeniger R;Acar AE;Mordhorst S;Suriano J;Irwin P;Warner RS;Gray K;Smith M .Acid/epoxy reaction catalyst screening for low temperature (120 degrees C) powder coatings[J].Progress in Organic Coatings: An International Review Journal,2005(2):98-109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%