3 mm thick 400 MPa grade ultrafine grained ferritic steel plates were bead-on-plate welded by CO2 laser with heat input of 120～480 J/mm. The microstructures of the weld metal mainly consist of bainite, which form is lower bainite plates or polygonal ferrite containing quantities of dispersed cementite particles, mixed with a few of low carbon martensite laths or ferrite, depending on the heat input. The hardness and the tensile strength of the weld metal are higher than those of the base metal, and monotonously increase as the heat input decreases. No softened zone exists inheat affected zone (HAZ). Compared with the base metal, although the grains of laser weld are much larger, the toughness of the weld metal is higher within a large range of heat input. Furthermore, as the heat input increases, the toughness of the weld metal rises to a maximum value, at which point the percentage of lower bainite is the highest, and then drops.
参考文献
| [1] | ASato.[J].Proc of Ultrasteel Tsukuba Japan,2001 |
| [2] | YWeng.[J].Proc of Ultrasteel Tsukuba Japan,2000:11. |
| [3] | W P Lee.[A].Tsukuba, Japan,2000:33. |
| [4] | NYurioka .[J].Welding in the world,1997,43(02):2. |
| [5] | Ksang;W Y Kim.[J].Welding Journal,2002:174. |
| [6] | XudongZHANG;Wuzhu CHEN;Ceng WANG .[J].Applied Lasers,2000,20(03):104. |
| [7] | WChen;Y Peng;C Wang;G Bao and Z Tian.[M].Proc of Int Symposium on Ultrafine Grained Steels Fukuoda Japan,2001:252. |
| [8] | YPeng;C Wang;W Chen.[C].Proc of Int Session of Workshop on New Generation Steel Beijing China,2001:199-206. |
| [9] | YPeng;C Wang;W Chen;G Bao, L Zhao and Z Tian.[M].Proc of the 4th Workshop on the Development of High Performance Structural Steels for 21st Century Fukuoka Japan,2002:299. |
| [10] | ChengWang .[D].Ph D Thesis Tsinghua University,2002. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%