先用共沉淀法制备了含有一定莫尔比的金属元素的氢氧化物沉淀,然后用热解氢氧化物沉淀的方法制备了石榴石薄膜,其晶粒尺寸在10~20 nm之间.通过对不同温度下合成的Bi-YIG薄膜的分析及测试,发现晶粒的大小在10~20 nm之间,法拉第旋转角和磁光优质分别可达3.6*104o/cm和6.7°.从X射线衍射(XRD)中可以看出,直接制备的纳米颗粒和Bi-YIG薄膜都是单一的石榴石相,合成比较充分.

A new method of producing nanocrystalline high-Bi-content garnet films was introduced.The films composed of crystal grains with the size from 10 to 20 nm were successfully prepared by pyrolyzing coprecipitated hydroxide slurry.The Transmission electron microscope(TEM)images of hydroxide slurry and Bi-YIG particles at different pH value were got.The relationship between the size of finally obtained grains and the pH value was found.The Scanning electron microscope(SEM)images of Bi-YIG films were photographed,and the Bi-YIG films were tested with the X-ray diffraction.The influences of heat treatment temperature and time on the films' magneto-optical and optical properties were also investigated in detail.At the wavelength of 633nm,the maximum of the Faraday rotation and the figure of magneto-optical merit of the films reach 3.6*104o/cm and 6.7°respectively.

参考文献

[1] Yasumori A;Katsuyama T;Kameshima Y et al.[J].Sol-Gel Science and Technology,2000,19:237.
[2] Eeppler W R;Kryder M H .[J].Physical and Chemistry of Solids,1995,11:1479.
[3] Kucera M;Gerber R;Teggart B J .[J].Journal of Magnetism and Magnetic Materials,2000,219(02):241.
[4] Ma X Y .[J].Journal of Materials Science:Materials in Electronics,2000,11(06):351.
[5] Kim T Y;Hirano T;Kitamoto Y et al.[J].IEEE Transactions on Magnetics,2002,38(05):3240.
[6] Adachi N;Denysenkov V P;Khartsev S I et al.[J].Applied Physics,2000,88:2734.
[7] Kim T Y;Hirano T;Yamazaki Y et al.[J].Applied Physics,2003,93:7501.
[8] Odagawa K.;Nakagawa K. .Effects of heat treatment conditions and impurity doping on garnet films for M-O recording prepared by pyrolysis[J].IEEE Transactions on Magnetics,1990(5):1721-1723.
[9] Shimokawa K;Dohnomae H;Mukai T;Yamada H et al.[J].Magnetism and Materials,1996,154:271.
[10] Suzuki T;Sequeda F;Do H et al.[J].APPLIED PHYSICS,1990,67(09):4435.
[11] Itoh A;Nakagawa K .[J].Japanese Journal of Applied Physics,1992,31:790.
[12] Mizuno T;Gomi M .[J].IEEE Transactions on Magnetics,1986,22:1236.
[13] Kuroda C S;Taniyama;T Kitamoto Y et al.[J].IEEE Transactions on Magnetics,2001,37:2432.
[14] Kuroda CS;Hirano T;Yoshida K;Namikawa T;Yamazaki Y;Kim TY .Preparation of nano-sized Bi-YIG particles for micro optics applications[J].Electrochimica Acta,1999(21):3921-3925.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%