针对丙烯酸聚氨酯防腐蚀涂层在沿海大气环境使用中的问题,采用电化学阻抗谱（EIS）技术、数值分析技术,研究了40℃模拟海洋大气环境中涂层内水分的扩散过程。结果表明,涂层内水分的扩散过程的lnCc-t1/2曲线可分为两个阶段：线性增加阶段和缓慢增加阶段。计算得到第一阶段涂层中水分的扩散系数D为5.45×10-10 cm2/s。研究还发现,海洋大气环境下聚氨酯涂层老化过程大致可分为三个阶段：水渗透过程、涂层下金属腐蚀过程和涂层完全失效过程。
The degradation of wildly used acrylic polyurethane coating exposed to seawater atmosphere was investigated.The water diffusion process during coatings aging process was studied by EIS and numerical value analysis technique.The lnCc-t1/2 curves of acrylic polyurethane coating indicated that the coating capacitance（lnCc） presented two typical stages as the experimental time（t1/2） increased,the coating capacitance increased rapidly in the beginning time of test,and then tended to be a slow growth stage.According to the linear part of lnCc-t1/2 period,the water diffusion coefficient D is obtained and the value is 5.45×10-10cm2/s.It is found that the degradation process of acrylic polyurethane coating exposed to marine atmosphere can be divided into three periods,i.e.,the water permeation process,the corrosion process of metal substrate under coating and the complete failure period of coating.
参考文献
| [1] | 李晓明,张义新,冯辉霞,郭静威,李汉峰.聚氨酯涂料研究现状及发展[J].应用化工,2010(07):1091-1095. |
| [2] | 杨丽霞,李晓刚,程学群,邓洪达,张三平,林安.水、氯离子在丙烯酸聚氨酯涂层中的扩散传输行为[J].中国腐蚀与防护学报,2006(01):6-10. |
| [3] | 解瑞,朱承飞,高红,王晓钧.沿海大气环境中氯化橡胶涂层失效规律[J].腐蚀与防护,2010(08):623-626. |
| [4] | 张鉴清.评价有机涂层防护性能的EIS数据处理[J].腐蚀科学与防护技术,1994(04):318. |
| [5] | Zhang JT;Hu JM;Zhang JQ;Cao CN .Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS[J].Progress in Organic Coatings: An International Review Journal,2004(2):145-151. |
| [6] | Zhang JT;Hu JM;Zhang JQ;Cao CN .Studies of impedance models and water transport behaviors of polypropylene coated metals in NaCl solution[J].Progress in Organic Coatings: An International Review Journal,2004(4):293-301. |
| [7] | Hu JM.;Zhang JQ.;Cao CN. .Determination of water uptake and diffusion of Cl- ion in epoxy primer on aluminum alloys in NaCl solution by electrochemical impedance spectroscopy [Review][J].Progress in Organic Coatings: An International Review Journal,2003(4):273-279. |
| [8] | L.V.S. Philippe;S.B. Lyon;C. Sammon;J. Yarwood .Validation of electrochemical impedance measurements for water sorption into epoxy coatings using gravimetry and infra-red spectroscopy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(3):887-896. |
| [9] | F. Deflorian;L. Fedrizzi;S. Rossi;P. L. Bonora .Organic coating capacitance measurement by EIS: ideal and actual trends[J].Electrochimica Acta,1999(24):4243-4249. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%