为探索适合于微波冶金高温反应过程使用的耐高温、抗热震、低微波吸收率耐火材料,采用常压烧结法在不同温度合成了不同配比的堇青石-莫来石质耐火材料.采用XRD分析、三点弯曲法及Angilent阻抗分析等测试了烧结温度及配比对耐火材料物相组成、抗弯强度、抗热震性能及介电性能的影响规律.结果表明,随烧结温度由1400℃提高至1450℃,烧结样品中残留的刚玉相明显减少,耐火材料的体积密度、抗弯强度显著增大,吸水率和显气孔率数值则显著降低;1100℃保温后急速水冷4次和8次热震循环后,耐火材料的抗弯强度损失率分别为30%和50%;随烧结温度由1400℃提高至1450℃,不同配比样品的相对介电常数均呈现增高趋势,而介电损耗角正切值则显著下降.综合耐火材料对抗弯强度、介电性能、抗热震性能的要求,其最佳烧结温度为1450℃,堇青石和莫来石的最佳配比为1∶1.

To develop a kind of refractory material suitable for microwave metallurgy,cordierite-mullite refractory materials with different mixture ratios were synthesized by sintering at normal atmosphere and different temperatures.The effects of sintering temperature and mixture ratio on phase composition,bending strength,thermal shock resistance and dielectric properties were analyzed.The results show that the content of remnant corundum phase after sintering decreases with the increase of temperature from 1400 ℃ to 1450 ℃,the volumetric density,the bending strength and the relative dielectric constants increase,the water-absorbing capacity,the apparatus porosity and the dielectric dissipation decreases.The loss of bending strength after 4 times and 8 times of thermal shocks from 1100 ℃ to room temperature in flowing water is 30% and 50%,respectively.Considering the integrated requirements of bending strength,dielectric property and thermal shock resistance,the optimal sintering temperature of this refractory material is 1450 ℃ and the optimal ratio of cordierite and mullite is 1∶ 1.

参考文献

[1] 刘能生,彭金辉,张利波,张泽彪.微波技术在稀贵金属冶金中的研究应用进展[J].贵金属,2009(04):48-51,62.
[2] 李钒,张梅,王习东.微波在冶金过程中应用的现状与前景[J].过程工程学报,2007(01):186-193.
[3] S DAS;A K MUKHOPADHYAY;S DATTA .Prospects of microwave processing: An overview[J].Bulletin of Materials Science,2009(1):1-13.
[4] 陈津,赵晶,冯秀梅,刘金营,林原生.微波冶金耐火材料研究[J].工业加热,2006(03):56-60.
[5] 韩亚苓,张巍,潘斌斌,孙泰礼.Al2O3/堇青石陶瓷的制备和抗热震性能研究[J].沈阳工业大学学报,2007(04):380-384,391.
[6] I. Quintana-Alonso;S.P. Mai;N.A. Fleck .The fracture toughness of a cordierite square lattice[J].Acta materialia,2010(1):201-207.
[7] 马林,吕戌生,薛娜,刘民生.堇青石-莫来石复相陶瓷制备[J].西安建筑科技大学学报(自然科学版),2008(06):756-758.
[8] K. P. Murali;S. Rajesh;K. Stanly Jacob;Om Prakash;A. R. Kulkarni;R. Ratheesh .Preparation and characterization of cordierite filled PTFE laminates for microwave substrate applications[J].Journal of Materials Science. Materials in Electronics,2010(2):192-198.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%