对具有高饱和磁感应强度的1J22型Fe-Co软磁合金进行高温退火实验,并研究了其质量、磁性能随退火温度及时间的变化.结果表明,合金在500℃以下退火时,质量无明显增加且磁体磁性能并无降低；而当合金在500℃以上退火后,合金增重速率增加,且磁性能明显下降.当合金在600℃退火后,合金饱和磁感应强度Bs降至2178mT,矫顽力Hc增至76.1A/m.微观结构研究表明,高温退火后合金晶粒尺寸及形貌无明显变化,而合金表面完全生成Fe3O4.合金磁性能的降低是由氧化物的增多及杂质的引入造成的.
参考文献
| [1] | Ikuo Ohnuma;Hirotoshi Enoki;Osamu Ikeda .Phase equilibria in the Fe-Co binary system[J].Acta materialia,2002(2):379-393. |
| [2] | Zhu Q;Li L;Masteller M S et al.An increase of structural order parameter in Fe-Co-V soft magnetic alloy after thermal aging[J].Applied Physics Letters,1996,69:3917-3919. |
| [3] | R. S. Sundar;S. C. Deevi .Effect of heat-treatment on the room temperature ductility of an ordered intermetallic Fe-Co-V alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):164-169. |
| [4] | Chen Guojun;Li Maochang;Zhou Yuanlong.Metallic soft magnetic materials and applications[M].北京:冶金工业出版社,1986:165-171. |
| [5] | 毕晓昉,张善庆,朱芳镇,徐惠彬.真空与磁场热处理改善FeCo合金的软磁性能[J].北京航空航天大学学报,2004(10):944-948. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%