高强玻璃纤维具有质轻、高强、耐高温及性价比高等优异特性,广泛应用于复合材料领域.本文通过对不同B2O3含量的高强玻纤试样进行拉伸、侵蚀、粘度、红外等性能的测试,研究了B2O3含量对高强玻璃纤维各种性能的影响.结果表明在高强玻璃纤维中引入一定含量B2O3,提高了玻璃纤维的拉伸强度,降低了高温粘度,一定程度上改善了高强玻璃纤维的工艺性能和提高了力学性能.
参考文献
| [1] | 凌根华,李雯.浅谈高强玻璃纤维的发展和应用[J].玻璃纤维,2008(05):7-10. |
| [2] | 刘建勋,朱建勋,祖群.新型高强度玻璃纤维制备与性能研究[J].功能材料,2010(07):1290-1293. |
| [3] | 重庆国际复合材料有限公司 .一种高强度高模量玻璃纤维[P].中国,101597140A.2,2009-12-9. |
| [4] | 陈汉仪 .高强度玻璃纤维成分[P].CN:94111349.3,1995-12-27. |
| [5] | Ransom S;Harris T .Glass composition[P].US,3402055,1968-09-17. |
| [6] | Yoshio S .Glass composition with high elasticity and heat resistance[P].JP,58064243,1997-07-02. |
| [7] | M. Assarar;D. Scida;A. El Mahi;C. Poilane;R. Ayad .Influence of water ageing on mechanical properties and damage events of two reinforced composite materials: Flax-fibres and glass-fibres[J].Materials & design,2011(2):788-795. |
| [8] | 郭书良,段跃新,肇研,罗云烽.连续玻璃纤维增强热塑/热固性复合材料力学性能研究[J].玻璃钢/复合材料,2009(05):42-45. |
| [9] | Sara Y. Yu;Javier Garcia-Martinez;Wei Li;Geroge D. Meitzner;Enrique Iglesia .Kinetic, infrared, and X-ray absorption studies of adsorption, desorption, and reactions of thiophene on H-ZSM5 and Co/H-ZSM5[J].Physical chemistry chemical physics: PCCP,2002(7):1241-1251. |
| [10] | 宋晓岚;杨贯中 .钛钡硼硅酸盐玻璃结构的红外光谱研究[J].湖南大学学报,1998,25(04):46-50. |
| [11] | 王铁邦 .二氧化硅等材料的红外光谱学研究[D].南京大学,2004. |
| [12] | Mysen B;Virgo D;Seifert A .Relationships between properties and structure of aluminosilica-temelts[J].American Mineralogist,1985,70:88-105. |
| [13] | Boumaza, A;Favaro, L;Ledion, J;Sattonnay, G;Brubach, JB;Berthet, P;Huntz, AM;Roy, P;Tetot, R .Transition alumina phases induced by heat treatment of boehmite: An X-ray diffraction and infrared spectroscopy study[J].Journal of Solid State Chemistry,2009(5):1171-1176. |
| [14] | Sunirmal Jana;Angela Surca Vuk;Aparajita Mallick;Boris Orel;Prasanta Kumar Biswas .Effect of boron doping on optical properties of sol-gel based nanostructured zinc oxide films on glass[J].Materials Research Bulletin,2011(12):2392-2397. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%