Behavior of transversal crack notched on slab comer during vertical-horizontal rolling process was simula-ted by FEM. The crack tip stress in the whole rolling process was obtained. Influences of the friction coefficient, the initial crack size, the edger roll profile, and the groove fillet radii of grooved edger roll on crack tip stress were ana-lyzed. For vertical rolling, the tension stress appears at crack tip near the slab top surface and the compression stress appears at crack tip near the slab side surface for the flat edger roll; however, the compression stress appears at crack tip near the slab top surface and the tension stress appears at crack tip near the slab side surface in the exit stage for the grooved edger roll. For horizontal rolling, the tension stress appears at crack tip just at the exit stage for the flat edger roll, and the tension stress appears in whole rolling stage; the tension stress value near the slab side surface is much larger than that near the slab top surface for the grooved edger roll.
参考文献
| [1] | Nikaido H;Naoi T;Shibata K et al.Numerical Simulation of Width Spread of Dog-Bone Slab in Non-Steady Horizontal Rolling[J].Journal of the Japan Society for Technology of Plasticity,1984,25(277):129. |
| [2] | Xiong Shangwu;Liu Xianghua;Wang Guodong;Zhang Qiang .A three-dimensional finite element simulation of the vertical-horizontal rolling process in the width reduction of slab[J].Journal of Materials Processing Technology,2000(1/3):146-151. |
| [3] | Xiong Shangwu;Zheng Guifang;Liu Xianghua .Analysis of the non-steady state vertical-horizontal rolling process in roughing trains by the three-dimensional finite element method[J].Journal of Materials Processing Technology,2002(1/3):53-61. |
| [4] | Yu Hailiang;Liu Xianghua;Zhao Xianming;Y. Kusaba .FEM analysis for V-H rolling process by updating geometric method[J].Journal of Materials Processing Technology,2006(1/3):323-327. |
| [5] | 喻海良,刘相华,李长生.立辊孔型内倒角半径对轧件变形的影响[J].钢铁,2006(06):47-51. |
| [6] | Esa Ervasti;Ulf Stahlberg .Behaviour of longitudinal surface cracks in the hot rolling of steel slabs[J].Journal of Materials Processing Technology,1999(2/3):141-150. |
| [7] | Esa Ervasti;Ulf Stahlberg .transversal cracks and their behaviour in the hot rolling of steel slabs[J].Journal of Materials Processing Technology,2000(1/3):312-321. |
| [8] | Nobuki Yukawa;Takashi Ishikawa;Yoshinori Yoshida et al.Influence of Rolling Condition on Deformation of Surface MicroDefect in Plate Rolling (in Japanese)[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,2005,91(12):861. |
| [9] | J. H. Chen;Q. Wang;G. Z. Wang;Z. Li .Fracture behavior at crack tip - a new framework for cleavage mechanism of steel[J].Acta materialia,2003(7):1841-1855. |
| [10] | LIU Xiang-hua;YU Hai-liang;LI Chang-sheng.Behavior of Corner Surface Cracks in V-H Rolling Process of Steel Slabs[A].France:Paris,2006:38. |
| [11] | YU Hai-liang,LIU Xiang-hua,LI Chang-sheng,Y. Kusaba.Behavior of Transversal Crack on Slab Corner During V-H Rolling Process[J].钢铁研究学报（英文版）,2006(06):31-37. |
| [12] | WANG Yan-bo.Metal-Plasric Working:Theory and Technology of Roiling[M].北京:冶金工业出版社,1988 |