采用混合气体(80％ Ar+ 20％ CO2)保护焊,对一种Ti-Nb微合金化控轧控冷高强钢板进行了焊接强度实验研究.通过微观组织特征分析,阐述了焊接接头热影响区(HAZ)的软化行为,综合分析了回火态HAZ的脆化机理.结果表明,随焊接热输入增加,粗晶热影响区(CGHAZ)晶粒长大,内部析出相粒子发生回溶现象,接头强度降低;焊接接头回火态强度有所提高,但随回火温度上升,CGHAZ的冲击韧性严重降低,其原因主要与原始组织遗传及碳化物沿晶界析出有关.
参考文献
| [1] | 李杏娥,赵志毅,薛润东,杨晓臻,谢建新.Ti在热轧高强带钢中的析出相与性能关系的研究[J].钢铁,2008(06):70-73. |
| [2] | 贺信莱;尚成佳;杨善武.高性能低贝氏体钢:成分、工艺、组织、性能与应用[M].北京:冶金工业出版社,2008 |
| [3] | Moon J;Lee J;Lee C .Prediction for the austenite grain size in the presence of growing particles in the weld HAZ of Ti-microalioyed steel[J].Materials Science and Engineering A,2007,459(1-2):40-46. |
| [4] | Akselsen O M;Grong O;Ryum N et al.HAZ grain growth mechanisms in welding of low carbon microalloyed steels[J].ACTA METALLURGICA,1986,34(09):1807-1815. |
| [5] | Joonoh Moon;Changhee Lee .Behavior of (Ti, Nb)(C, N) complex particle during thermomechanical cycling in the weld CGHAZ of a microalloyed steel[J].Acta materialia,2009(7):2311-2320. |
| [6] | 康永林,陈庆军,王克鲁,孙浩,于浩.700MPa级低碳贝氏体钢的热处理工艺研究[J].材料热处理学报,2005(03):96-99. |
| [7] | 张楠,董现春,张熹,陈延清,章军.钛微合金化SQ700MCD高强钢粗晶热影响区软化的原因[J].机械工程材料,2012(04):88-92. |
| [8] | 董现春,张楠,陈延清,张熹.高Ti，Nb析出强化高强钢接头强度及焊接热影响区软化行为分析[J].焊接学报,2012(11):72-76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%