加载氧化试验表明:Ni3Al合金表层氧化物在加载时以NiO为主,不加载氧化时以Al2O3为主。本文讨论了这一现象对Ni3Al氧化环境敏感脆化的影响,并通过在热力学分析中引入氧化体积变化对这一现象的本质进行了探索。
The present test shows that tensile stress has a significant influence on the oxidation behavior of Ni_3Al. NiO is predominant in the oxide scale of Ni3Al when the oxidation proceeds with tensile stress, while Al2O3 is predominant when oxidation proceeds