Effect of Direct Ageing Treatment on Stress-Rupture Properties of GH761 Alloy

钢铁研究学报(英文版), 2008, 15(3): 61-64.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China;Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

2.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

3.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China;Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

4.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

5.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China

6.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

基金项目: 国家自然科学基金(50271072;50471083)

Effect of Direct Ageing Treatment on Stress-Rupture Properties of GH761 Alloy

YANG Shu-lin ^1, , SUN Wen-ru ^2, , LIU Fang ^3, , GUO Shou-ren ^4, , YANG Hong-cai ^5, , HU Zhuang-qi ^6,

1.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China;Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

2.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

3.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China;Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

4.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

5.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China

6.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China

Keywords： direct ageing treatment

The effect of direct ageing treatment on microstrueture and stress-rupture properties of GH761 alloy was studied. Phosphorus was added to the tested alloy for its beneficial effect on stress-rupture life. It was found that the grain size of the tested alloy became much finer after direct ageing treatment, in comparison with the commercial GH761 alloy under standard heat treatment condition. The optimum direct ageing treatment has been determined as follows: 830 ℃× 4 h, air cooling+720 ℃× 24 h, air cooling. After such treatment, the higher stress-rupture prop-erties of the test alloy at 650 ℃, 690 MPa were obtained. The role of phosphorus is still effective under the condition of direct ageing treatment.

参考文献

[1]	SUN Wen-ru .Effect of P,S and Si on the Solidification,Segregation and Mechanical Properties in GH761 Alloy[D].沈阳:中国科学院金属研究所,1993.
[2]	HU Zhuang-qi;SUN Wen-ru;GUO Shou-ren .Effect of P,S and Si on the Solidification,Microstrueture and Properties in Fe-Ni Base Superalloys[J].Acta Metallurgica Sinica(English Letters),1996,9:443.
[3]	SUN Wen-ru;GUO Shou-ren;LU De-zhong et al.Effect of Phosphorous on the Microstructure and Stress-Rupture properties in an Fe-Ni-Cr Base Superalloys[J].Metallurgical and Materials Transactions,1997,28A:649.
[4]	胡壮麒,孙文儒,郭守仁,卢德忠.微量元素磷在铁镍基变形高温合金中的作用[J].中国有色金属学报,2001(06):947-959.
[5]	杨树林,孙文儒,郭守仁,魏志刚,杨洪才,胡壮麒.磷对GH761合金力学性能的影响[J].金属学报,2005(12):1249-1255.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Effect of Direct Ageing Treatment on Stress-Rupture Properties of GH761 Alloy

参考文献