对在饱和Ca(OH)2溶液中养护至不同龄期的粉煤灰进行测试,对粉煤灰中氧化硅、氧化铝等成分的溶解速率、粉煤灰颗粒表面的微观形貌以及反应产物进行了分析,同时,对SO42--在钙矾石AFt晶体的形成过程中的影响也进行了探讨.结果表明:在饱和Ca(OH)2溶液体系中,粉煤灰中活性SiO2和Al2 O3的溶出速率要比粉煤灰水泥浆体中的火山灰反应快;经饱和Ca(OH)2溶液处理后,粉煤灰颗粒表面主要有4种形貌——碱刻蚀现象、结构致密层、疏松的沉积层、颗粒表面形成钙矾石晶体;SO42-的浓度影响钙矾石的成核结晶.
参考文献
| [1] | Malhotra V;Mehta P.Pozzolanic and cementitious materials (advance in concrete technology)[M].USA:Gordon &Breach Publishers,1996:11. |
| [2] | Alonso J;Wesche K.Fly ash in concrete[M].London:E and FN Spon,1991:3. |
| [3] | Wang A et al.Fly ash effects:Ⅲ.The microaggregate effect of fly ash[J].Cement and Concrete Research,2004,34(11):2061. |
| [4] | Takemoto K;Uchikawa H.Hydration of pozzolanic cement[A].Paris,France,1980:1. |
| [5] | Neville A.Properties of concrete[M].Essex,UK:Longman Group Limited,1995:845. |
| [6] | Papadakis V;Fardis M et al.Hydration and carbonation of pozzolanic cements[J].ACI MATERIALS JOURNAL,1992,89(2):119. |
| [7] | Fraay A;Bijen J;Haan Y .The reaction of fly ash in concrete:A critical examination[J].Cement and Concrete Research,1989,19(2):235. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%