采用金相显微镜、透射电镜对中国低活化马氏体钢(CLAM)在500℃长期时效过程中的显微组织变化规律进行研究.结果表明,随着时效时间的延长,金相组织和晶粒尺寸均没有发生明显变化；马氏体板条随着保温时间的延长几乎没有变化,经过1000h时效后宽度仍然保持了时效前的约400nm.析出物发生了一定程度的长大,经过1000h时效后析出物最大尺寸约为160nm.
参考文献
| [1] | Griffin R D;Dodd R A;Kulcinski G L et al.The effect of tempering and aging on a low activation martensitic steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1990,21(07):1853. |
| [2] | Kphyama A;Hishinuma A;GellesD S et al.Low-activaiton ferritic and martensitic steels for fusion application[J].Journal of Nuclear Materials,1996,233-237:138. |
| [3] | Klueh RL.;Gelles DS.;Jitsukawa S.;Kimura A.;Odette GR.;van der Schaaf B.;Victoria M. .Ferritic/martensitic steels - overview of recent results[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2002(Pt.a):455-465. |
| [4] | 黄群英,李春京,李艳芬,刘少军,吴宜灿,李建刚,万发荣,巨新,单以银,郁金南,朱升云,张品源,杨建锋,韩福生,孔明光,李合琴,室贺健夫,长坂琢也.中国低活化马氏体钢CLAM研究进展[J].核科学与工程,2007(01):41-50,85. |
| [5] | 赵飞,万奎贝,乔建生,万发荣,马纪东,许咏丽,吴宜灿.低活化马氏体钢的微观结构与力学性能[J].核科学与工程,2007(01):59-63. |
| [6] | 乔建生,姚昊,黄依娜,万发荣.硅对CLAM钢微观结构和力学性能的影响[J].原子能科学技术,2009(10):915-920. |
| [7] | Sakasegawa H.;Hirose T.;Kohyama A.;Katoh Y.;Harada T.;Asakura K. Kumagai T. .Effects of precipitation morphology on toughness of reduced activation ferritic/martensitic steels[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2002(Pt.a):490-494. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%