A new type of high strength steel containing a significant amount of stable retained austenite was obtained by austempering immediately after intercritical annealing. This sort of low carbon steel only contains alloying elements of silicon and manganese rather than nickel and chromium. Its mechanical properties were enhanced considerably due to strain-induced martensite transformation and transformation-induced plasticity (TRIP) of retained austenite when it was strained at temperatures between Ms and Md, because retained austenite was moderately stabilized due to carbon enrichment by austempering. Austempering was carried out at different temperatures and 400 ℃ was found to be optimal. Tensile strength, total elongation and strength-ductility balance reached the maximum values and the product of tensile strength and total elongation exceeded 30 135 MPa % when the TRIP steel was held at 400 ℃ and strained at 350 ℃.
参考文献
| [1] | M. De MEYER .The Influence of the Substitution of Si by Al on the Properties ofCold Rolled C-Mn-Si TRIP Steels[J].ISIJ International,1999(8):813-822. |
| [2] | Zackay V F;Rker E R;Fahr D .The Enhancement of Ductilityon High-Strength Steels[J].Transactions ASM,1967,60:252-259. |
| [3] | Sakuma Y;Tsumura O;Kechi H .Mechanical Properties andRetained Austenite in Intercritically Heat-Treated Bainite-Transformed Steel and Their Variation With Si and Mn Addi-tions[J].Metallurgical and Materials Transactions,1991,22(02):489-498. |
| [4] | Sugimoto K.;Sakaguchi J. .Stretch-flangeability of a High-strength TRIP Type Bainitic Sheet Steel[J].ISIJ International,2000(9):920-926. |
| [5] | Seung Chul BAIK;Seongju KIM;Young Sool JIN .Effects of Alloying Elements on Mechanical Properties and Phase Transformation of Cold Rolled TRIP Steel Sheets[J].ISIJ International,2001(3):290-297. |
| [6] | Sugimoto K;Usui N;Kobayashi M et al.Effects of VolumeFraction and Stability of Retained Austenite on Ductility ofTRIP-Aided Dual-Phase Steels[J].ISIJ International,1992,32(12):1311-1318. |
| [7] | Sugimoto K I;Misu M;Kobayashi M .Effects of Second PhaseMorphology on Retained Austenite Morphology and TensileProperties in a TRIP-Aided Dual-Phase Steel Sheet[J].ISIJ International,1993,33(07):775-782. |
| [8] | A. Zarei HANZAKI;P. D. HODGSON;S. YUE .Hot Deformation Characteristics of Si-Mn TRIP Steels with and without Nb Microalloy Additions[J].ISIJ International,1995(3):324-331. |
| [9] | J. MAHIEU;J. MAKI;B.C. De COOMAN .Phase Transformation and Mechanical Properties of Si-Free CMnAl Transformation-Induced Plasticity-Aided Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(8):2573-2580. |
| [10] | Bhadeshla H K D H;Edmonds D V .The Bainite Transforma-tion in a Silicon Steel[J].Metallurgical and Materials Transactions,1979,10(07):895-907. |
| [11] | Gilmour J B;Purdy G R;Kirkaldy J S .ThermodynamicsControlling the Proeutectoid Ferrite Transformations in Fe-C-Mn Alloys[J].Metallurgical and Materials Transactions,1972,3:1455. |
| [12] | Radcliffe S V;Schatz M .The Effect of High Pressure on theMartensitic Reaction in Iron-Carbon Alloys[J].Acta Materialia,1962,10:201. |
| [13] | Speich G R;Demarest V A;Miller R L .Formation of Aus-tenite During Intercritical Annealing of Dual-Phase Steels[J].Metallurgical and Materials Transactions,1981,12:1419. |
| [14] | Choi I D;Bruce D M;Kim S J .Deformation Behavior of LowCarbon TRIP Sheets at High Strain Rates[J].ISIJ International,2002,42(12):1483. |
| [15] | JIAJUN WANG;SYBRAND VAN DER ZWAAG .Stabilization Mechanisms of Retained Austenite in Transformation-Induced Plasticity Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(6):1527-1539. |
| [16] | Kim S J;Lee C G;Choi I et al.[J].Metallurgical and Materials Transactions,2001,32(03):505-514. |
| [17] | Jacques P J;Ladriere J;Delannay F .On the Influence of In-teractions between Phase on the Mechanical Stability of Re-tained Austenite in Transformation-Induced Plasticity Multi-phase Steels[J].Metallurgical and Materials Transactions,2001,32:2759-2768. |
| [18] | Pyshmintsev I Y;Meyer M D;Cooman B C D .[J].Metallurgical and Materials Transactions,2002,33:1659-1667. |
| [19] | Sugimoto K I;Kobayashi M;Hashimoto S I .Ductility andStrain-Induced Transformation in a High-Strength Transfor-mation-Induced Plasticity-Aided Dual-Phase Steel[J].Metallurgical and Materials Transactions,1992,23(11):3085-3091. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%