在酒石酸-硫酸溶液中阳极氧化AA2099-T8铝锂合金获得阳极氧化膜,并采用新型绿色封闭工艺对阳极氧化膜进行封孔处理.采用场发射扫描电镜观察阳极氧化膜封孔前后的显微形貌,通过开路电位、动电位极化、电化学阻抗谱及中性盐雾实验研究氧化膜封孔前后的耐腐蚀性能.结果表明:采用酒石酸-硫酸阳极氧化处理能在AA2099-T8铝锂合金表面生成一层均匀、致密的氧化膜,采用新型封闭工艺可在常温下有效封闭氧化膜孔隙;阳极氧化和封孔处理均能提高合金的抗腐蚀能力,但单纯的阳极氧化对合金耐腐蚀性能的提高有限,而阳极氧化+封孔处理能显著提高合金的耐腐蚀性能.
参考文献
| [1] | 宋利康;廖建华;郑堂介;张建东;朱永国.大飞机铝锂合金等直段研制关键技术[J].航空制造技术,2015(4):82-85. |
| [2] | 李劲风;刘平礼;陈永来;张绪虎;郑子樵.Mg、Ag、Zn多元复合微合金化Al-（3.2～3.8）Cu-（1.0～1.4）Li合金的显微组织和力学性能[J].中国有色金属学报（英文版）,2015(7):2103-2112. |
| [3] | 麻彦龙;孟晓敏;黄伟九;张小彬.显微组织的非均匀性对AA2099-T8铝锂合金局部腐蚀的影响[J].中国有色金属学报,2015(3):611-617. |
| [4] | Arenas MA;de Damborenea JJ.Surface characterisation of cerium layers on galvanised steel[J].Surface & Coatings Technology,20042/3(2/3):320-325. |
| [5] | 刘建华;李永星;于美;李松梅;孙玉静.己二酸铵对7075-T6铝合金硫酸阳极氧化的影响[J].中国有色金属学报,2012(1):324-330. |
| [6] | Hakimizad, A.;Raeissi, K.;Ashrafizadeh, F..Characterization of aluminum anodized layers modified in sulfuric and phosphoric acid baths and their effect on conventional electrolytic coloring[J].Surface & Coatings Technology,20128/9(8/9):2438-2445. |
| [7] | 杜楠;王帅星;赵晴;邵志松.硼酸对7050铝合金硼酸-硫酸阳极氧化膜结构及耐蚀性的影响[J].中国有色金属学报（英文版）,2012(7):1655-1660. |
| [8] | M. Curioni;P. Skeldon;E. Koroleva.Role of Tartaric Acid on the Anodizing and Corrosion Behavior of AA 2024 T3 Aluminum Alloy[J].Journal of the Electrochemical Society,20094(4):C147-C153. |
| [9] | V. Marzocchi;L. Iglesias-Rubianes;G.E. Thompson.THE INFLUENCE OF TARTARIC ACID ADDITIONS ON THE ANODIZING BEHAVIOUR OF AA2024-T3 ALLOY IN SULPHURIC ACID[J].Corrosion reviews,20073/4(3/4):461-473. |
| [10] | Y. Ma;X. Zhou;G.E. Thompson;M. Curioni;X. Zhong;E. Koroleva;P. Skeleton;P. Thomson;M. Fowles.Discontinuities in the porous anodic film formed on AA2099-T8 aluminium alloy[J].Corrosion Science,201112(12):4141-4151. |
| [11] | Y. Ma;X. Zhou;G. E. Thompson;M. Curioni;P. Skeldon;X. Zhang;Z. Sun;C. Luo;Z. Tang;F. Lu.Anodic film growth on Al-Li-Cu alloy AA2099-T8[J].Electrochimica Acta,2012:148-159. |
| [12] | Y. Ma;X. Zhou;G.E. Thompson;P. Skeldon.Surface texture formed on AA2099 Al-Li-Cu alloy during alkaline etching[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013Jan.(Jan.):292-299. |
| [13] | Y. Ma;X. Zhou;G. E. Thompson.Microstructural Modification Arising from Alkaline Etching and Its Effect on Anodizing Behavior of Al-Li-Cu Alloy[J].Journal of the Electrochemical Society,20133(3):C111-C118. |
| [14] | Leszek Zaraska;Grzegorz D. Sulka;Janusz Szeremeta;Marian Jaskula.Porous anodic alumina formed by anodization of aluminum alloy (AA1050) and high purity aluminum[J].Electrochimica Acta,201014(14):4377-4386. |
| [15] | S. Theohari;Ch. Kontogeorgou.Effect of temperature on the anodizing process of aluminum alloy AA 5052[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013Nov.1(Nov.1):611-618. |
| [16] | M. Garcia-Rubio;M. P. de Lara;P. Ocon;S. Diekhoff;M. Beneke;A. Lavia;I. Garcia.Effect of postreatment on the corrosion behaviour of tartaric-sulphuric anodic films[J].Electrochimica Acta,200921(21):4789-4800. |
| [17] | M. SAEEDIKHANI;M. JAVIDI;A. YAZDANI.2024-T3铝合金在硫酸-硼酸-磷酸中的阳极氧化和腐蚀行为[J].中国有色金属学报（英文版）,2013(09):2551-2559. |
| [18] | A.VENUGOPAL;Rajiv PANDA;Sushant MANWATKAR;K.SREEKUMAR;L.RAMA KRISHNA;G.SUNDARARAJAN.微弧氧化处理对AA7075铝合金在3.5％ NaCl溶液中局部腐蚀行为的影响[J].中国有色金属学报（英文版）,2012(03):700-710. |
| [19] | V. R. Capelossi;M. Poelman;I. Recloux;R. P. B. Hernandez;H. G. de Melo;M. G. Olivier.Corrosion protection of clad 2024 aluminum alloy anodized in tartaric-sulfuric acid bath and protected with hybrid sol-gel coating[J].Electrochimica Acta,2014:69-79. |
| [20] | 李英东;张优;李松梅;赵丕植.己二酸对2024铝合金阳极氧化成膜和耐蚀性能的影响[J].中国有色金属学报（英文版）,2016(2):492-500. |
| [21] | 刘建华;李永星;于美;李松梅;陈高红;于海洋.三种无铬封闭方法对铝合金阳极氧化膜耐蚀性的影响[J].材料热处理学报,2011(10):129-133. |
| [22] | 贾睿程 .铝合金AA2024、AA6061和AA7075电化学腐蚀行为[D].内蒙古科技大学,2012. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%