利用液相还原两步法,油酸为萃取荆和保护剂,葡萄糖和次亚磷酸钠将五水硫酸铜分别还原为氧化亚铜和单质铜,制备得到了粒度为50～100nm左右分散均匀的球形纳米铜颗粒,并用XRD、SEM和TEM对其进行了表征.结果表明,在油酸的保护下,采用液相还原两步法可制得分散性好、具有抗氧化性能的球形纳米铜颗粒.
参考文献
| [1] | 张志梅,古乐,齐毓霖,梁风.纳米级金属粉改善润滑油摩擦性能的研究[J].润滑与密封,2000(02):40,37. |
| [2] | Boccuzzi F et al.[J].Catalysis Today,2002,75(1-4):169-175. |
| [3] | Zhao Hongsheng et al.[J].International Journal of Adhesion and Adhesives,Z007,Z7(06):429-433. |
| [4] | Lee B et al.[J].Current Applied Physics,2009,9(2Supplement 1):157-160. |
| [5] | Wu Songping;Jiao Li;Ni Jing .Preparation of ultra fine copper-nickel bimetallic powders for conductive thick film[J].Intermetallics,2007(10):1316-1321. |
| [6] | Joshi S S et al.[J].NanoStructured Materials,1998,10(07):1135-1144. |
| [7] | 吕伟,吴莉莉,徐润春,吴佑实,盖红德,邹科.二维纳米结构--氧化铋纳米片的制备与表征[J].山东大学学报（工学版）,2008(01):109-112. |
| [8] | Capek, I .Preparation of metal nanoparticles in water-in-oil (w/o) microemulsions[J].Advances in Colloid and Interface Science,2004(1/2):49-74. |
| [9] | Pfeifer P et al.[J].Applied Catalysis A:General,2005,286(02):175-185. |
| [10] | 姜敏.水热法制备单质铜[J].宝鸡文理学院学报（自然科学版）,2005(04):277-279. |
| [11] | 王士平,程继贵,宋鹏,万磊.溶胶-凝胶法制备超细Mo-Cu粉末及性能表征[J].粉末冶金材料科学与工程,2009(03):189-194. |
| [12] | 康仕芳,刘爱民,张猛.化学沉淀法制备超细粉体过程行为[J].化学工业与工程,2005(05):346-349. |
| [13] | 朱协彬,段学臣.超声电解法制备纳米铜粉的研究[J].上海有色金属,2004(03):97-99. |
| [14] | Luo Yonglan .[J].Materials Letters,2008,62:3758-3760. |
| [15] | Wu Songping et al.[J].Materials Letters,2006,60:2438-2442. |
| [16] | Jian-guang Yang;Yuang-lin Zhou;Takeshi Okamoto .Preparation of Oleic Acid-capped Copper Nanoparticles[J].Chemistry Letters,2006(10):1190-1191. |
| [17] | Li Z Y;Gong P W;Zhai Y C .[J].Journal of Iron and Steel Research International,2007,14:126. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%