在不同温度和电流密度的条件下,制备不锈钢基PbO2电极,分析了电极的析氧曲线及析氧动力学参数,进而考察了温度和电流密度对PbO2电极节能性和电催化活性的影响.结果表明:温度为80℃,电流密度为30mA/cm2时,制备的电极成分稳定,重现性好,可有效降低槽电压,电催化活性良好;在小电流密度下的主要产物为β-PbO2,大电流密度下生成部分α-PbO2;与传统的铅基阳极材料相比,该PbO2电极节能性和催化活性均有较大程度的提高.
参考文献
| [1] | 王彦军,谢刚,杨大锦,李永佳,肖婷蔓.降低电积锌直流电耗的现状分析[J].湿法冶金,2005(04):208-211. |
| [2] | 吕少祥,戴曦.降低锌电积直流电耗生产实践[J].有色金属(冶炼部分),2001(06):13-15,26. |
| [3] | A.B.Velichenko;D.Devilliers .Electrodeposition of fluorine-doped lead dioxide[J].Journal of Fluorine Chemistry,2007(4):269-276. |
| [4] | Panic VV;Jovanovic VM;Terzic SI;Barsoum MW;Jovic VD;Dekanski AB .The properties of electroactive ruthenium oxide coatings supported by titanium-based ternary carbides[J].Surface & Coatings Technology,2007(2):319-324. |
| [5] | Zhao Q.;Liu Y.;Muller-Steinhagen H.;Liu G. .Graded Ni-P-PTFE coatings and their potential applications[J].Surface & Coatings Technology,2002(2/3):279-284. |
| [6] | Yuehai Song;Gang Wei;Rongchun Xiong .Structure and properties of PbO{sub}2-CeO{sub}2 anodes on stainless steel[J].Electrochimica Acta,2007(24):7022-7027. |
| [7] | 司云森,杨显万.电化学极化过程实验数据处理分析的研究[J].昆明理工大学学报(理工版),2003(01):164-167. |
| [8] | 任秀斌,陆海彦,刘亚男,李伟,林海波.钛基二氧化铅电极电沉积制备过程中的立体生长机理[J].化学学报,2009(09):888-892. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%