探索了采用三步法制备液芯磁性微囊的新方法.采用喷雾法制备了磁性海藻酸钙微球,用激光粒度仪测得微球平均粒径为130/μm.通过合成脲甲醛树脂对磁性海藻酸钙微球进行包覆,详细研究了脲甲醛预聚和缩聚条件对包覆结果的影响.最后对脲甲醛树脂包覆后的磁性海藻酸钙微球进行液化,结果表明,在一段时间内,液化效果受柠檬酸钠溶液浓度和pH值影响明显;最终微囊液化效果良好,体积增大,内部的磁性粒子向囊心集聚.
参考文献
| [1] | 宋健;陆磊;李效军.微胶囊化技术及应用[M].北京:化学工业出版社,2001:23. |
| [2] | 曹阳,秦炜.磁性聚苯乙烯微球的制备与性能研究[J].离子交换与吸附,2005(05):437-443. |
| [3] | 谢钢,张和鹏,张秋禹,李铁虎.细乳液聚合法制备磁性复合微球及其表征[J].高分子学报,2003(05):626-630. |
| [4] | 龚涛,汪长春.具有核壳结构磁性复合微球的制备与表征[J].高分子学报,2008(11):1037-1042. |
| [5] | Bahar Tahsin;Celebi Serdar S. .Immobilization of glucoamylase on magnetic poly(styrene) particles[J].Journal of Applied Polymer Science,1999(1):69-73. |
| [6] | Yamaura M;Camilo R L;Sampaio L C et al.Preparation and characterization of (3-aminopropyl) triethoxysilane-coated magnetite nanoparticles[J].Journal of Magnetism and Magnetic Materials,2004,279:210. |
| [7] | Maria Mikhaylova;Do Kyung Kim;Catherine C.Berry;Andrei Zagorodni;Muhammet Toprak;Adam S.G.Curtis;Mamoun Muhammed .BSA Immobilization on Amine-Functionalized Superparamagnetic Iron Oxide Nanoparticles[J].Chemistry of Materials,2004(12):2344-2354. |
| [8] | 丁小斌;孙宗华;万国详.磁性高分子微球的制备和应用研究进展[J].化学通报(印刷版),1997(01):1. |
| [9] | Koo HY;Chang ST;Choi WS;Park JH;Kim DY;Velev OD .Emulsion-based synthesis of reversibly swellable, magnetic nanoparticle-embedded polymer microcapsules[J].Chemistry of Materials: A Publication of the American Chemistry Society,2006(14):3308-3313. |
| [10] | 葛艳蕊,冯薇.原位聚合法制备玫瑰香精微胶囊的研究[J].日用化学工业,2003(05):337-339. |
| [11] | 马萍,祝力,孙淑英,梁冬梅.海藻酸钙凝胶微球的制备和pH依赖性溶胀[J].中国海洋药物,2003(05):35-37. |
| [12] | 王康,何志敏.海藻酸微胶囊的制备及在药物控释中的研究进展[J].化学工程,2002(01):48-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%