以Mg-6％Zn合金为基体、β-Ca3(PO4)2为强化相,采用粉末冶金工艺制备Mg-6％Zn-10％(β-Ca3(PO4)2)复合材料.利用光学显微镜观察复合材料的显微组织,采用X射线衍射仪分析相组成,采用压缩试验评估复合材料力学性能,采用动电位极化法和浸泡实验研究复合材料在模拟体液(SBF)中的腐蚀行为.结果表明:β-Ca3(PO4)2在烧结过程中与基体合金没有发生明显反应；复合材料密度为1.936g/cm3,压缩强度为339 MPa,弹性模量为24GPa;添加β-Ca3(PO4)2可降低Mg-6％Zn在SBF中的腐蚀速度；Mg-6％Zn-10％(β-Ca3(PO4)2)复合材料在SBF中的电化学腐蚀速度为2.277 mm/y,浸泡30 d的浸泡腐蚀速度为2.133 mm/y,SBF的pH值随着浸泡时间的延长而上升,最终稳定在10.
参考文献
| [1] | Serre CM;Papillard M;Chavassieux P;Voegel JC;Boivin G .Influence of magnesium substitution on a collagen-apatite biomaterial on the production of a calcifying matrix by human osteoblasts.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1998(4):626-633. |
| [2] | Hideyuki Kuwahara;Yousef Al-Abdullat;Naoko Mazaki .Precipitation of Magnesium Apatite on Pure Magnesium Surface during Immersing in Hank's Solution[J].Materials transactions,2001(7):1317-1321. |
| [3] | 戴尅戎.骨折内固定与应力遮挡效应[J].医用生物力学,2000(02):69-71. |
| [4] | Staiger MP;Pietak AM;Huadmai J;Dias G .Magnesium and its alloys as orthopedic biomaterials: A review[J].Biomaterials,2006(9):1728-1734. |
| [5] | El Rahman SS .Neuropathology of aluminum toxicity in rats (glutamate and GABA impairment).[J].Pharmacological research: The official journal of The Italian Pharmacological Society,2003(3):189-194. |
| [6] | NAKAMURA Y;TSUMURA Y;TONOGAI Y;SHIBAYA T ITO Y .Differences in behavior among the chlorides of seven rare earth elements administered intravenously to rats[J].Fundamental and Applied Toxicology,1997,37(02):106-116. |
| [7] | Witte F;Kaese V;Haferkamp H;Switzer E;Meyer Lindenberg A;Wirth CJ;Windhagen H .In vivo corrosion of four magnesium alloys and the associated bone response.[J].Biomaterials,2005(17):3557-3563. |
| [8] | SONG G L .Control of biodegradation of biocompatible magnesium alloys[J].Corrosion Science,2007,49(04):1696-1701. |
| [9] | Zheng YF;Gu XN;Xi YL;Chai DL .In vitro degradation and cytotoxicity of Mg/Ca composites produced by powder metallurgy.[J].Acta biomaterialia,2010(5):1783-1791. |
| [10] | Zhang S;Zhang X;Zhao .Research on an Mg-Zn alloy as a degradable biomaterial.[J].Acta biomaterialia,2010(2):626-640. |
| [11] | Witte F;Feyerabend F;Maier P;Fischer J;Stormer M;Blawert C;Dietzel W;Hort N .Biodegradable magnesium-hydroxyapatite metal matrix composites.[J].Biomaterials,2007(13):2163-2174. |
| [12] | COELHO P G;COIMBRA M E;RIBEIRO C;FANCIO E,HIGA O,SUZUKI M,MARINCOLA M .Physico/chemical characterization and preliminary human histology assessment of a β-TCP particulate material for bone augmentation[J].Materials Science and Engineering C,2009,29(07):2085-2091. |
| [13] | Kokubo T;Takadama H .How useful is SBF in predicting in vivo bone bioactivity?[J].Biomaterials,2006(15):2907-2915. |
| [14] | American Society for Testing and Materials.Annual Book of ASTM Standards[M].Philadelphia,PA:American Society for Testing and Materials,2004 |
| [15] | Effect of heat treatment on corrosion behaviour of magnesium alloy AZ91D in simulated body fluid[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(3):1035. |
| [16] | SONG G L;ATRENS A;STJOHN D H;NAIRN J LI Y .The electrochemical corrosion of pure magnesium in 1 N NaCl[J].Corrosion Science,1997,39(05):855-875. |
| [17] | Li Z;Gu X;Lou S;Zheng Y .The development of binary Mg-Ca alloys for use as biodegradable materials within bone.[J].Biomaterials,2008(10):1329-1344. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%