在500℃的锌液中,对Fe-B共晶合金进行恒温静态腐蚀试验.对其腐蚀动力学和基体/Zn腐蚀界面进行研究,探讨了Fe-B共晶合金在锌液中的腐蚀过程和机理.结果表明,Fe-B共晶合金有比较好的耐锌液腐蚀性能;锌液腐蚀基体的过程是Fe原子和Zn原子相互扩散的过程;扩散导致新相的形成,在热应力和锌液冲击应力以及新相生长的拉应力的作用下,腐蚀层产生裂纹断裂并溶解.腐蚀以此方式反复进行,最终导致合金失效.
参考文献
| [1] | M. X. Yao;J. B. C. Wu;R. Liu .Microstructural characteristics and corrosion resistance in molten Zn-Al bath of Co-Mo-Cr-Si alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):299-305. |
| [2] | W.J. Wang;J.P. Lin;Y.L. Wang .The corrosion of intermetallic alloys in liquid zinc[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):237-243. |
| [3] | K. Zhang .Wear of cobalt-based alloys sliding in molten zinc[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/6):545-555. |
| [4] | 艾桃桃,王芬,陈平.金属间化合物的制备方法及应用[J].稀有金属快报,2006(01):5-12. |
| [5] | 李永梅,马瑞娜,曹晓明,范永哲.纯铁和Fe-Al金属间化合物在液锌中的腐蚀研究[J].热加工工艺,2009(08):1-3,6. |
| [6] | 张艺,李洪波,刘俊友.硅对铁基合金耐液锌腐蚀的影响[J].腐蚀与防护,2009(10):704-707. |
| [7] | B. Yao;W. H. Su;F. S. Li;B. Z. Ding;Z. Q. Hu .Phase transition from Fe3B to Fe2B under high pressure[J].Journal of Materials Science Letters,1997(24):1991-1993. |
| [8] | 钟凤兰.正交结构的Fe3B电子理论[J].吉林大学自然科学学报,1997(04):49-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%