采用正交试验法筛选了一种以植酸、钼酸钠和缓蚀添加剂为基本组成的无铬钝化液。通过电化学阻抗谱测试，确定了最佳成膜时间；通过5％CusO4。点滴试验、10％NaCl浸泡试验和极化曲线测试，对电沉积镀镍层无铬钝化后的耐蚀性能进行了研究。结果表明，采用本无铬钝化工艺后，镀镍层耐蚀性能良好。
In order to improve the corrosion resistance of electrodeposited nickel coating and subsititute the carcinogenic hexavalent chromium passivation, a new chromate free passivation solution was screened out by means of orthogonal analysis experiments. Fhe solution was composed of phytic acid, sodium molybdate and corrosion inhibitor. The optimal time for conversion film formation was determined by electrochemical impedance spectroscopy. The corrosion resistant properties of electrodeposited nickel coating were studied by dropping corrosion test in 5% CuSO4, immersion test in 10% NaC1 and polarization curves. The results showed that the film passivated by the technology has good anti-corrosion performance.
参考文献
| [1] | 唐甜,潘勇,周益春.碱锰电池钢壳用镀镍钢带的力学和耐腐蚀性能[J].电池,2005(05):380-381. |
| [2] | 张宝根.钢基镀镍层保护材料的研制[J].电镀与精饰,1995(01):13. |
| [3] | 胡会利,陈丽姣.表面转化膜无铬化技术的研究动向[J].腐蚀与防护,2009(10):727-731,755. |
| [4] | Zhao M;Wu SS;Luo JR;Fukuda Y;Nakae H .A chromium-free conversion coating of magnesium alloy by a phosphate-permanganate solution[J].Surface & Coatings Technology,2006(18/19):5407-5412. |
| [5] | Mamas S;Kiyak T;Kabasakaloglu M;Koc A .The effect of benzotriazole on brass corrosion[J].Materials Chemistry and Physics,2005(1):41-47. |
| [6] | Han Keping;Jing Li Fang .Decorative and Protective Conversion Films on Nickel Plate[J].Metal finishing,1996(6):97-99. |
| [7] | 方景礼.NT-1镀镍防变色工艺研究[J].材料保护,1992(09):16. |
| [8] | 徐群杰,齐航,周小晶,周国定.新型绿色缓蚀剂植酸的研究进展[J].腐蚀与防护,2009(02):75-77. |
| [9] | 张荣发,巢强花,赵芳,王为,聂新兵,周冲,张洪,胡长员,朱光宇.植酸在镁合金防护中的应用现状[J].材料工程,2008(11):71-74. |
| [10] | 徐瑞东,王军丽,薛方勤,郭忠诚.镍磷合金镀层防变色性能初探[J].腐蚀与防护,2004(06):260-262. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%