研究了NiAl-30.9Cr-3Mo-0.1Dy合金在1300 K～1500 K空气中的恒温氧化行为.结果表明:NiAl-30.9Cr-3Mo-0.1Dy合金的抗氧化性远优于NiAl-31Cr-3Mo合金;1500 K的氧化动力学曲线基本遵循抛物线关系,在1350 K～1450 K的氧化动力学曲线符合立方抛物线关系,1300K的氧化动力学曲线则符合5次方关系.氧化过程中,合金的表面生成了连续致密的Al2O3氧化膜:稀土元素的活性作用以及Al2O3与基体合金之间的富Cr层的形成,提高了Al2O3的粘附能力.Dy的添加也减少了NiAl相上Al2O3的生成量,延缓了θ-Al2O3向α-Al2O3相的转变时间.
参考文献
| [1] | Guo J T;Cui C Y;Chen Y X et al.[J].Intermetallics,2001,9:287. |
| [2] | Young E W A;Dewit J H W .[J].Solid State Ionics,1986,16:39. |
| [3] | Prescott R;Mitchell D F;Sproule G I et al.[J].Solid State Ionics,1992,53:229. |
| [4] | Jedlinski J;Borchardt G .[J].Oxidation of Metals,1991,36:317. |
| [5] | Nesbitl J A;Lowell C E.[A].Pittsburgh,PA:MRS,1993:107. |
| [6] | 张光业,张华,郭建亭,李志军.Dy对NiAl-31Cr-3Mo合金循环氧化性能的影响[J].稀有金属,2005(06):845-850. |
| [7] | Cui C Y;Chen Y X;Guo J T et al.[J].Materials Letters,2000,43(5-6):303. |
| [8] | Wang F H;Lou H Y;Wu W T .[J].Oxidation of Metals,1995,43:395. |
| [9] | XIN Li;LI Mei-shuan;ZHOU Long-jiang .Influences of Yttrium on Adhesion of Oxide Scale of Fe-Cr-Al Alloy[J].Journal of Rare Earths,2001(2):117-121. |
| [10] | 徐春梅,郭建亭.NiAl微晶涂层对两种NiAl基共晶合金高温氧化性能的影响[J].金属学报,2002(07):673-678. |
| [11] | Wang F H .[J].Oxidation of Metals,1997,47:247. |
| [12] | JIN Hui-ming;ZHANG Lin-nan;LI Mei-shuan .Rare Earth Effects on Adhesion of Cr2O3 Oxide Scale formed on Surface of Co-40Cr Alloy[J].Journal of Rare Earths,2001(1):34-39. |
| [13] | Rybicki G C S;Smialek J L .[J].Oxidation of Metals,1989,32:275. |
| [14] | Ui-Hamid A .[J].Oxidation of Metals,2001,58(1-2):22. |
| [15] | 李美栓.金属的高温腐烛[M].北京:冶金工业出版社,2001:263. |
| [16] | 张永刚;韩雅芳;陈国良.结构材料与金属间化合合物[M].北京:国防工业出版社,2001:534. |
| [17] | Mahaton K H.The Science and Technology of Materials[M].北京:科学出版社,1999:529. |
| [18] | Zou Z H.The Science and Technology of Materials[M].北京:科学出版社,1999:22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%