简述了锆合金氧化膜的物相组成和转变及其对锆合金耐腐蚀性能的影响.并重点论述了锆合金的化学成分、热处理制度、表面改性技术及工作条件对锆合金氧化膜和耐腐蚀性能的影响.
参考文献
[1] | 赵文金,周邦新,苗志,彭倩,蒋有荣,蒋宏曼,庞华.我国高性能锆合金的发展[J].原子能科学技术,2005(z1):2-9. |
[2] | 刘文庆,李强,周邦新,姚美意.水化学对Zr-4合金氧化膜/基体界面处压应力的影响[J].稀有金属材料与工程,2004(10):1112-1115. |
[3] | Lin Jianlong;Li Hualong;Szpunar J A et al.Analysis of zirconium oxide formed during oxidation at 623K on Zr-2.5Nb and Zircaloy-4[J].Materials Science and Engineering,2004,338:104. |
[4] | Pecheur D;Godlewski J;Peybernes J et al.Contribution to the understanding of the effect of the water chemistry on the oxidation kinetics of zircaloy-4 cladding[J].ASTM Special Technical Publication,2000,1354:793. |
[5] | 周邦新,李强,黄强.水化学对锆合金耐腐蚀性能影响的研究[J].核动力工程,2000(05):439. |
[6] | 刘文庆,周邦新,李强,姚美意.不同介质对Zr-4合金氧化膜结构的影响[J].稀有金属材料与工程,2005(04):562-564. |
[7] | Li Hualong;Glavicic M G;Szpunar J A .A model of texture formation in ZrO2 films[J].Materials Science and Engineering,2004,366(A):164. |
[8] | Beie H J;Mitwalsky A;Garzarolli F et al.Examinations of the corrosion mechanism of zirconium alloys[J].ASTM Special Technical Publication,1994,1245:615. |
[9] | Godlewski J .How the tetragonal zirconia is stabilized in the oxide scale that is formed on a zirconium alloy corroded at 400℃ in steam[J].ASTM Special Technical Publication,1994,1245:663. |
[10] | 薛祥义,白新德,田振业,周青山,刘建章.锆合金疖状腐蚀研究综述[J].稀有金属材料与工程,2004(09):902-906. |
[11] | Yueh HK.;Cox B. .Luminescence properties of zirconium oxide films[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2003(1):57-67. |
[12] | Bozzano PB;Ramos C;Saporiti F;Vazquez PA;Versaci RA;Saragovi C .Oxidation of the hexagonal Zr(Cr0.4Fe0.6)(2) Laves phase[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2004(2/3):225-231. |
[13] | Saporiti F;Bozzano P;Versaci R et al.Characterization of the Laves phases Zr(Cr,Fe)2 oxidized in an open furnace using mossbauer spectroscopy[J].Hyperfine Interactions,2002,139-140(1-4):379. |
[14] | Cong Li;Rulin Zuo;Zhongkui Li;Shihao Ying;Baoluo Shen .Transmission electron microscopy investigation of Zr_2(Fe,Ni) particles incorporated in the oxide film formed on a Zirconium alloy[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2004(2):272-276. |
[15] | Yueh HK.;Cox B. .Cathodoluminescence imaging of oxidised zirconium alloys[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2004(2/3):203-214. |
[16] | Zhou Bangxin;Zhao Wenjin;Miao Zhi.The effect of heat treatment on the corrosion behavior of zircaloy-4[A].北京:原子能出版社,1996:104. |
[17] | Kim Tae Kyu;Choi Byung Seon;Jeong Yong Hwan 等.退火处理对Ti-Al-Zr合金拉伸性能和腐蚀行为的影响[J].国外核动力,2003,24(01):44. |
[18] | Urbanic V F;Griffiths M .Micro structural aspects of corrosion and hydrogen ingress in Zr-2.5Nb[J].ASTM Special Technical Publication,2000,1354:641. |
[19] | Kim Hyun Gil;Jeong Yong Hawn;Kim To Hoon .Effect of isothermal annealing on the corrosion behavior of Zr-xNb alloys[J].Journal of Nuclear Materials,2004,326(2-3):125. |
[20] | 赵文金,苗志,蒋有荣,蒋宏曼,周邦新.预生氧化膜处理对锆-4包壳疖状腐蚀的影响[J].稀有金属,2000(02):150-153. |
[21] | Xiaoyang Liu,Xinde Bai.Effect of lanthanum ion implantation on oxidation behavior of zircaloy[J].北京科技大学学报(英文版),2004(03):260-262. |
[22] | Peng DQ.;Bai XD.;Chen XW.;Zhou QG.;Liu XY.;Yu RH. .Influence of molybdenum ion implantation on the aqueous corrosion behavior of zircaloy-4[J].Surface & Coatings Technology,2003(2/3):291-297. |
[23] | Peng DQ.;Bai XD.;Chen XW.;Zhou QG.;Liu XY.;Yu RH. .Effect of cerium ion implantation on the aqueous corrosion behavior of zircaloy-4[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):7-11. |
[24] | 彭德全,白新德,陈小文,周庆刚,刘晓阳,余任泓.钇和铈离子注入纯锆的腐蚀行为研究[J].稀有金属材料与工程,2004(09):918-923. |
[25] | Zhao Yalin;Liu Jianzhang .The Effect of laser surface treatment on the nodular corrosion of zircaloy-4[J].Rare Metal Materials and Engineering,1996,25(04):44. |
[26] | 刘文庆,李强,周邦新,姚美意.LiOH水溶液加速Zr-4合金腐蚀的研究[J].稀有金属材料与工程,2004(07):728-730. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%