为了提高白炭黑与橡胶的相容性,同时防止防老剂的挥发,采用γ-缩水甘油醚氧丙基三甲氧基硅烷与对氨基二苯胺(PPDA)的反应物对白炭黑进行表面改性,得到表面接枝防老剂的白炭黑.将改性白炭黑应用于天然橡胶(NR)中考察其增强与防老性能,并与炭黑/NR、未改性白炭黑/NR和Si69改性白炭黑/NR复合材料相比较(均添加防老剂4020).结果表明,改性白炭黑/NR复合材料的焦烧时间延长,硫化时间缩短,白炭黑在橡胶中的分散性提高,同时具备更出色的力学性能.随着表面接枝防老剂含量的增加,改性白炭黑/NR复合材料的拉伸强度和撕裂强度比未改性白炭黑和Si69改性白炭黑/NR均有大幅提高.当接枝的PPDA含量达到5.27％(与白炭黑的质量比)时,其拉伸强度比未改性白炭黑/NR提高了90％,比Si69改性白炭黑/NR提高了73％,并接近炭黑/NR;其撕裂强度是未改性白炭黑/NR的5倍,Si69改性白炭黑/NR的2.5倍,炭黑/NR的2倍.另外,表面接枝防老剂的白炭黑/NR复合材料具有优异的抗热氧、抗臭氧和湿热老化性能;其抗臭氧老化性能优于添加通用防老剂4020的对比复合材料.
参考文献
| [1] | 李剑波,杜孟成,郑崇纳,等.绿色轮胎用白炭黑的研发方向[J].橡胶科技市场,2009,7(12):10-12.Li Jianbo,Du Mengcheng,Zheng Chongna,et al.Development trend of silica for green tire[J].China Rubber Science and Technology Market,2009,7(12):10-12. |
| [2] | Wolff S,Gǒrl U,Wang M J,et al.Silica-based tread compounds[J].European Rubber Journal,1994,176(1):16-19. |
| [3] | Hair M L,Hertl W.Acidity of surface hydroxyl groups[J].The Journal of Physical Chemistry,1970,74(1):91-94. |
| [4] | Hockey J A,Pethica B A.Surface hydration of silicas[J].Transactions of the Faraday Society,1961,57:2247-2262. |
| [5] | 徐苏华,古菊,罗远芳,等.纳米微晶纤维素对白炭黑/天然橡胶复合材料性能的影响[J].复合材料学报,2011,28(6):39-44.Xu Suhua,Gu Ju,Luo Yuanfang,et al.Influence of nanocrystalline cellulose on SiO2/natural rubber composites[J].Acta Materiae Compositae Sinica,2011,28(6):39-44. |
| [6] | Ansarifar A,Wang L,Ellis R J,et al.Enhancing the mechanical properties of styrene-butadiene rubber by optimizing the chemical bonding between silanized silica nanofiller and the rubber[J].Journal of Applied Polymer Science,2007,105(2):322-332. |
| [7] | Yan H X,Tian G H,Sun K,et al.Effect of silane coupling agent on the polymer-filler interaction and mechanical properties of silica-filled NR[J].Journal of Polymer Science,Part B:Polymer Physics,2005,43(5):573-584. |
| [8] | Sulekha P B,Joseph R,Manjooran K B.New oligomer-bound antioxidants in natural rubber/polybutadiene rubber and natural rubber/ styrene-butadiene rubber blends[J].Journal of Applied Polymer Science,2004,93(1):437-443. |
| [9] | Angert L G,Zenchenko A I,Kuzminskii A S.Volatilization of phenyl-2-naphthylamine from rubber[J].Rubber Chemistry and Technology,1961,34(3):807-815. |
| [10] | Spacht R B,Hollingshead W S,Bullard H L,et al.Volatility of antioxidants and antiozonants Ⅰ:Pure compounds in absence of rubber[J].Rubber Chemistry and Technology,1964,37(1):210-220. |
| [11] | Th(o)rnblom K,Palmlf M,Hjertberg T.The extractability of phenolic antioxidants into water and organic solvents from polyethylene pipe materials-Part 1[J].Polymer Degradation and Stability,2011,96(10):1751-1760. |
| [12] | Sulekha P B,Joseph R,George K E.Studies on polyisobutylene bound paraphenylene diamine antioxidant in natural rubber[J].Polymer Degradation and Stability,1999,63(2):225-230. |
| [13] | Sulekha P B,Joseph R,Madhusoodanan K N,et al.New oligomer-bound antioxidant for improved flex crack resistance and ozone resistance[J].Polymer Degradation and Stability,2002,77(3):403-416. |
| [14] | Sulekha P B,Joseph R,Prathapan S.Synthesis and characterization of chlorinated paraffin wax-bound paraphenylenediamine antioxidant and its application in natural rubber[J].Journal of Applied Polymer Science,2001,81(9):2183-2189. |
| [15] | Liauw C M,Allen N S,Edge M,et al.The role of silica and carbon-silica dual phase filler in a novel approach to the high temperature stabilization of natural rubber based composites[J].Polymer Degradation and Stability,2001,74(1):159-166. |
| [16] | El-Wakil A E A,Barakat M A.Study of the effect of natural rubber-graft-o-aminophenol on the thermal stability and mechanical properties of nitrile rubber[J].Journal of Applied Polvmer Science,2011,119(4):2461-2467. |
| [17] | 丁著明,刘丽湘,王 玲.反应型聚合物稳定剂的研究进展[J].精细与专用化学品,2006,14(11):5-9.Ding Zhuming,Liu Lixiang,Wang Ling.Research progress on reactive stabilizers for polymers[J].Fine and Specialty Chemicals,2006,14(11):5-9. |
| [18] | Pan Q W,Wang B B,Chen Z H,et al.Reinforcement and antioxidation effect of antioxidant functionalized silica in styrene-butadiene rubber[J].Materials & Design,2013,50:558-565. |
| [19] | Bertora A,Castellano M,Marsano E,et al.A new modifier for silica in reinforcing SBR elastomers for the tyre industry[J].Macromolecular Materials and Engineering,2011,296:455-464. |
| [20] | Payne A R.The dynamic properties of carbon black-loaded natural rubber vulcanizates[J].Journal of Polymer Science,1962,6(19):57-62. |
| [21] | Payne A R,Whittaker R E.Low strain dynamic properties of filled rubbers[J].Rubber Chemistry and Technology,1971,44(2):440-478. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%