用乳液聚合合成的较窄相对分子质量分布的高相对分子质量支化聚苯乙烯(BPS)改性聚碳酸酯(PC),与线型聚苯乙烯(LPS)改性PC进行对比.研究了共混物的流变性能、力学性能和热性能.结果表明,BPS的加入可显著降低基体PC的熔体黏度,改善PC加工流动性,且在保持PC优良热性能的同时,明显提高PC的断裂伸长率、拉伸强度、弯曲强度等力学性能;而在相同质量分数的情况下,PC/LPS共混体系的黏度远大于PC/BPS共混体系的黏度,部分力学性能和热性能较PC基本保持不变,断裂伸长率则明星下降.
参考文献
| [1] | C.Gao;D.Yan .Hyperbranched polymers:from synthesis to applications[J].Progress in Polymer Science,2004(3):183-275. |
| [2] | Yang, HJ;Jiang, BB;Huang, WY;Zhang, DL;Kong, LZ;Chen, JH;Liu, CL;Gong, FH;Yu, Q;Yang, Y .Development of Branching in Atom Transfer Radical Copolymerization of Styrene with Triethylene Glycol Dimethacrylate[J].Macromolecules,2009(16):5976-5982. |
| [3] | Nunez CM.;Guo RK.;Baskir JN.;Morgan DR.;Andrady AL. .Mechanical properties of blends of PAMAM dendrimers with poly(vinyl chloride) and poly(vinyl acetate)[J].Journal of Polymer Science, Part A. Polymer Chemistry,1998(12):2111-2117. |
| [4] | 李少杰,黄文艳,席秉云,薛小强,杨宏军,蒋必彪.星形聚苯乙烯改性聚碳酸酯[J].高分子材料科学与工程,2013(08):84-87. |
| [5] | 王士峰,黄文艳,薛小强,江力,蒋必彪.链转移剂单体合成支化聚苯乙烯及其表征[J].高分子材料科学与工程,2012(02):16-19. |
| [6] | Jiang, L.;Huang, W.;Xue, X.;Yang, H.;Jiang, B.;Zhang, D.;Fang, J.;Chen, J.;Yang, Y.;Zhai, G.;Kong, L.;Wang, S. .Radical polymerization in the presence of chain transfer monomer: An approach to branched vinyl polymers[J].Macromolecules,2012(10):4092-4100. |
| [7] | 郭金龙,黄文艳,张俊,薛小强,杨宏军,蒋必彪.链转移剂单体α-甲基丙烯酸-3-巯基己酯对支化聚苯乙烯悬浮聚合的影响[J].高分子材料科学与工程,2013(08):93-96,100. |
| [8] | Massa DJ.;Turner SR.;Voit BI.;Shriner KA. .NOVEL BLENDS OF HYPERBRANCHED POLYESTERS AND LINEAR POLYMERS[J].Macromolecules,1995(9):3214-3220. |
| [9] | 赵宝辉,巴信武,侯文龙,王素娟,韩颖慧.超支化聚（酰胺-酯）/聚氯乙烯共混体系流变性能及其力学性能研究[J].高分子材料科学与工程,2003(02):157-160. |
| [10] | Lee JS;Quirk RP;Foster MD .Synthesis and characterization of well-defined, regularly branched polystyrenes utilizing multifunctional initiators[J].Macromolecules,2005(13):5381-5392. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%