针对碳纤维在碳／碳烧蚀防热复合材料中应用的基础问题，论述了不同碳纤维结构、成分、表面特征，及其力学性能和热物理性能的高温演变规律，揭示了碳纤维灰分含量对碳纤维力学性能和热氧化性能的影响。确定了在碳／碳复合材料复合成型过程中，碳纤维结构受基体碳影响的变化规律和碳纤维表面特征对碳／碳材料宏观力学性能的影响。阐明了碳／碳复合材料中碳纤维的力学性能对纤维发生折断烧蚀的阻碍作用和通过控制碳／碳成型最高温度实现提高性能的途径。
To resolve the basic application problems of carbon fibers in ablative heat protection composites, the high temperature revolution of the structures, elemental contents and surface features of carbon fibers were discussed and their mechanical and thermal physical properties were also given. The influence of ash content on the mechanical and anti-oxidation properties of carbon fibers was disclosed. The microstructure development of carbon fibers, influenced by carbon matrix, was determined during the formation process of C/C composites. The mechanical performance of C/C composite was influenced by the surface features of the carbon fibers used as the raw materials. The carbon fibers with high mechanical performance can prevent their fracture during ablation. By control the maximum heat-treat temperature during the man- ufacture of C/C composites, their mechanical performance can be increased.
参考文献
| [1] | Buckley J D;Edie D D.Carbon-Carbon Materials and Composites[M].New Jersey:Noyes Publications,1993:42-43. |
| [2] | Kohno T;Mutoh A;Kude Y.Potential Qualities of Pitch-Based Carbon Fiber for High Temperature Composites[A].Florida:John Wiley 8 Sons,Inc,1994:162-169. |
| [3] | Za|divar R J;Rellick G S;Yang J M .Fiber Strength Utilization in Carbon/Carbon Composites:Part II.Extended Studies with Pitch-and PAN-Based Fibers[J].Journal of Materials Research,1995,10(03):609-624. |
| [4] | Zaldivar RJ.;Yang JM.;Rellick GS. .FAILURE MODES OF A UNIDIRECTIONAL ULTRA-HIGH-MODULUS CARBON-FIBER CARBON-MATRIX COMPOSITE[J].Journal of the American Ceramic Society,1995(3):623-632. |
| [5] | Mochizuki C;Kimura Y .Evaluation of Oxidation Behaviors and Mechanical Properties of C/C Composite with Two Different of Types Carbon Fiber[J].Journal of the Society of Materials Sci-ence,2000,49(08):892-898. |
| [6] | Chung D D L.Carbon Fiber Composites[M].Bostun:Butter-worth-Heinemann,1994:65-75. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%