ZA27 alloy was prepared by casting with permanent mold and then annealed at 250℃for 1-4h.The damping capacity of the alloy was measured using a testing apparatus based on the cantilever beam technique. It was found that the as-cast ZA27 alloy possesses high damping capacity with the value of 1.3 × 10-3 at 320Hz. After annealed at 250℃ for 1h, the damping capacity decreases to 1.1 × 10-3 and then remains constant even when the annealing time is increased to 4h. The microstructure of the as-cast ZA27 alloy consists of large dendrites of Al-rich primary α-phases, eutectoid (α + η) and nonequilibrium eutectic phases (α + η + ε). After annealing at 250℃ for 1h, the ε phase disappears due to dissolution into the matrix, and the spacing between the flakes of eutectoid increases. The further increase in the annealing time has little effect on the spacing. The damping mechanism of the alloy was discussed considering the thermoelastic damping and defect damping. The value of thermoelastic damping accounts only for 7%-8% in the overall damping in cantilever beam damping measurements and the damping capacity of the ZA27 alloy came mainly from defect damping.
参考文献
| [1] | WANG Jin-cheng,ZHANG Zhong-ming,YANG Gen-cang.Numerical modeling of damping capacity of Zn-Al alloys with fully lamellar microstructures[J].中国有色金属学会会刊（英文版）,2005(05):1049-1054. |
| [2] | Y Z Zhao;Q Gao;H Wang .[J].Materials for Mechanical Engineering,2005,29(02):30. |
| [3] | Z M Zhang;J C Wang;G C Yang;Y.H.Zhou .[J].Journal of Materials Science,2000,35(13):3383. |
| [4] | X F Zhu;J P Shui .[J].A cra Physica Sinica,1996,45(06):1010. |
| [5] | 张忠明,刘宏昭,王锦程,徐源,杨根仓.金属材料阻尼性能测试系统[J].西安理工大学学报,2000(02):133-137. |
| [6] | J M Zhang;R J Perez;C R Wong;E.J.Lavernia .[J].Materials Science and Engineering R:Reports,1994,13(08):325. |
| [7] | A S Nowick;B S Berry.Anelastic Relaxation in Crystalline Solids[M].New York:Academic Press,Inc,1972:501. |
| [8] | I G Ritchie;Z L Panzl;F E Goodwin .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22:617. |
| [9] | E Gervais;R J Barnhurst;C A Loong.[J].Journal of Metals,1985(11):43. |
| [10] | 张忠明,徐春杰,王锦程,刘宏昭.热挤压铸态ZA27合金阻尼性能研究[J].功能材料,2005(04):529-531. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%