采用SEM、TEM和XRD等测试方法,研究了一种Ni-Cr-W合金经不同温度(1230~1300 ℃)和不同时间(10~120 min)固溶处理后的显微组织.结果表明:经过固溶处理后,合金的析出相为富W的面心立方M6C和富Cr面心立方的M23C6.随着固溶温度升高和保温时间延长,碳化物体积分数降低.在1270 ℃, 120 min时,大部分的碳化物溶解进入基体,孪晶处的碳化物首先发生溶解.M6C与基体不存在任何位向关系,晶界上析出的M23C6(220)晶面与基体(1-31)晶面的夹角为30°.

The microstructure features of a kind of Ni-Cr-W superalloy after solution heat treatment at different temperatures (1230-1300 °C) for various time (10-120 min) were investigated by means of scanning electron microscope (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The results show that the precipitated phases of the alloy after solution heat treatment are identified as W-rich fcc M6C and Cr-rich fcc M23C6 carbides. The volume fraction of carbides decreases with increasing of the solution heat treatment temperature and time. At the temperature above 1270 °C for 120 min, most of carbides are dissolved into the Ni-matrix, and the carbides distributing at twin boundaries may be dissolved into the matrix first. M6C carbide has no any fixed orientation relationship with the Ni-matrix, but the angle of M23C6 (220) to the matrix (1-31) is 30°.

参考文献

[1] Furuya Kazuo;Yamamoto Takashi;Kainuma Toshio et al.[J].Transactions of the Iron and Steel Institute of Japan,1985,25(03):249.
[2] Kurata Yuji;Tsuji Hirokazu;Masami Shindo et al.[J].Journal of Nuclear Materials,1997,246:196.
[3] Fujio A;Tatsuhlko T .[J].Zeitschrift fur Metallkunde,1985,76:479.
[4] Watanabe Rikizo;Chiba Yoshitaka .[P].U nitedS tatesPatent,No.4006015,1977.
[5] Kondo Tatsuo;Nakijima Hajime;Shindo Masami .[P].United States Patent,No.5141704,1992.
[6] Klarstrom Dwaine L .[P].United States Patent,No.4476091,1984.
[7] Choi Ju;Lee Chong K;Kyunggi-do .[P].United States Patent,No 4810466,1989.
[8] Choi Ju;Kim Hyon T .[P].U nitedS tatesPatent,No.5419869,1995.
[9] Tawancy H M .[J].Journal of Materials Science,1992,27:6481.
[10] Goldschmidt H J.Interstitial Alloys[M].Butterworth,London,1967
[11] Garofalo F;Domis W F;Von Gemmingen F .[J].Transactions of the Metallurgical Society of AIME,1964,230:1460.
[12] Liu L R;Jin T;Zhao N R et al.[J].Materials Sci and Eng A,2003,361:191.
[13] Koul A K;Pickering F B .[J].Acta Metallurgica,1982,30:1303.
[14] Koul A K;Gessinger G H .[J].ACTA METALLURGICA,1983,31:1061.
[15] Henry M F;Yoo Y S;Yoon D Y et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:1733.
[16] Lee S B;Yoon D Y;Henry M F.[A].Korea:Kyongju,1995:2373.
[17] Zhao J C;Larsen M;Ravikumar V .[J].Materials Sci and Eng A,2000,293:112.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%