以十六烷基三甲基溴化铵为分散剂、尿素为沉淀剂,通过水热法制备了前驱体MnCO3,经热处理得到MnO2.利用X射线衍射和扫描电子显微镜对材料的结构和形貌进行表征,结合循环伏安和恒流充放电测试材料的电化学性能.结果表明:二氧化锰呈现出立方体的结构,样品在-0.4～0.6V(vs.SCE)的电位范围内具有良好的电容性能和循环稳定性,在0.5 A/g的电流密度下单电极的放电比电容高达312.3 F/g.
参考文献
| [1] | 段立谦,李景印,李玉佩,何前国.新型纳米结构二氧化锰的制备及其超级电容性能[J].河北科技大学学报,2011(02):169-172. |
| [2] | Xueliang Li;Changlong Han;Xiangying Chen .Preparation and performance of straw based activated carbon for supercapacitor in non-aqueous electrolytes[J].Microporous and mesoporous materials: The offical journal of the International Zeolite Association,2010(1/3):303-309. |
| [3] | Yudong Zhu;Haoquan Hu;Wencui Li .Resorcinol-formaldehyde based porous carbon as an electrode material for supercapacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2007(1):160-165. |
| [4] | 李学良,何金铧,徐海龙.氧化镍的水热制备及超电容性能研究[J].金属功能材料,2011(05):58-61. |
| [5] | 张莹,刘开宇,张伟,王洪恩.二氧化锰超级电容器的电极电化学性质[J].化学学报,2008(08):909-913. |
| [6] | Kai Wang;Jiyong Huang;Zhixiang Wei .Conducting Polyaniline Nanowire Arrays for High Performance Supercapacitors[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2010(17):8062-8067. |
| [7] | 张传香 .超级电容器NiO/介孔碳复合电极材料的制备及其性能研究[D].南京航空航天大学,2008. |
| [8] | 汪形艳,王先友,胡传跃,李宪平,易涛.电沉积法制备超级电容器电极材料纳米MnO_2[J].湘潭大学自然科学学报,2009(04):47-51. |
| [9] | 徐小存,刘开宇,孙哲,蒋志军.界面法制备的纳米MnO_2的性能[J].电池,2009(06):301-303. |
| [10] | Yujuan Yang;Chengde Huang .Effect of synthetical conditions, morphology, and crystallographic structure of MnO2 on its electrochemical behavior[J].Journal of solid state electrochemistry,2010(7):1293-1301. |
| [11] | 马军,郑明森,董全峰.超级电容器用纳米二氧化锰的合成及其电化学性能[J].电化学,2007(03):233-237. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%