Precipitation Kinetics of Cr2N in High Nitrogen Austenitic Stainless Steel

钢铁研究学报(英文版), 2008, 15(6): 72-77.

^1, , ^2, , ^3, , ^4,

1.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

2.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

3.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

4.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

基金项目: 国家自然科学基金(50534010) 国家重点基础研究发展计划(973计划)(2004CB619103)

Precipitation Kinetics of Cr2N in High Nitrogen Austenitic Stainless Steel

SHI Feng ^1, , WANG Li-jun ^2, , CUI Wen-fang ^3, , LIU Chun-ming ^4,

1.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

2.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

3.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

4.School of Materials and Metallurgy,Northeastern University,Shenyang 110004,Liaoning,China

Keywords： high nitrogen austenitic stainless steel

The precipitation behavior of Cr2N during isothermal aging in the temperature range from 700℃to 950℃ in Fe-18Cr-12Mn-0.48N(in mass percent)high nitrogen austenitic stainless steel,including morphology and content of precipitate,was investigated using optical microscopy,scanning electron microscopy,and transmission electron microscopy.The isothermal precipitation kinetics curve of Cr2N and the corresponding precipitation activation energy were obtained.The results show that Cr2N phase precipitates in a cellular way and its morphology is transformed from initial granular precipitates to lamellar ones in the cell with increasing aging time.The nose temperature of Cr2N precipitation is about 800℃,with a corresponding incubation period of 30 min,and the ceiling temperature of Cr2N precipitation is 950℃.The diffusion activation energy of Cr2N precipitation is 296 kJ/mol.

参考文献

[1]	Dischino A;Kenny J M .Effect of Grain Size on the Corrosion Resistance of a High Nitrogen-Low Nickel Austenitic Stainless Steel[J].Journal of Materials Science Letters,2002,21(24):1969.
[2]	Vanderschaeve F;Taillard R;Foct J .Discontinuous Preeipitation of Cr2N in a High Nitrogen,Chromium-Manganese Austenitic Stainless Steel[J].Journal of Materials Science,1995,30(23):6035.
[3]	Lee T H;Oh C S;Lee C G et al.Precipitation of o-Phase in High-Nitrogen Austenitic 18Cr-18Mn-2Mo-0.9N Stainless Steel During Isothermal Aging[J].Scripta Materialia,2004,50(10):1325.
[4]	Kikuchi M;Kaiihara M;Choi S K .Cellular Precipitation Involving Both Substitutional and Interstitial Solutes:Cellular Precipitation of Cr2N in Cr-Ni Austenitic Steels[J].Material Science and Engineering,1991,146A(1-2):131.
[5]	Lee T.H.;Kim S.J. .Crystallographic Details of Precipitates in Fe-22Cr-21 Ni-6Mo-(N) Superaustenitic Stainless Steels Aged at 900 deg C[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(7):1713-1723.
[6]	YUAN Zhi-zhong;CHEN Kang-min;DAI Qi-xun et al.Study on Cr2N-Phase Precipitation Along Intercrstanine of High Nitrogen Austenitic Steels[J].Heat Treatment of Metals,2004,29(03):37.
[7]	Knutsen R D;Lang C I;Basson J A .Discontinuous Cellular Precipitation in a Cr-Mn-N Steel With Niobium and Vanaeliam Additions[J].Acta Materialia,2004,52(08):2407.
[8]	N. C. Santhi Srinivas;V. V. Kutumbarao .On the discontinuous precipitation of Cr2N in Cr-Mn-N austenitic stainless steels[J].Scripta materialia,1997(3):285-291.
[9]	F. Shi,L.J. Wang,W.F. Cui,C.M. Liu.PRECIPITATION BEHAVIOR OF M2N IN A HIGH-NITROGEN AUSTENITIC STAINLESS STEEL DURING ISOTHERMAL AGING[J].金属学报（英文版）,2007(02):95-101.
[10]	XIAo Ji-mei.Alloy Phase and Phase Transformation[M].北京:冶金工业出版社,1987:187.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Precipitation Kinetics of Cr2N in High Nitrogen Austenitic Stainless Steel

参考文献