概述了近年来热镀锌钢筋的研究及实际应用结果,分析了热镀锌钢筋的耐腐蚀机理,介绍了热镀锌钢筋的工艺性能、力学性能,及其与混凝土基体的结合性能等,指出了今后的研究方向.
The results of the research and application on hot-dip galvanized rebar in concrete in recent years were summarized. The corrosion resistance mechanism of hot-dip galvanized rebar was analyzed. The process properties and mechanical properties of hot-dip galvanized rebar and its binding properties with concrete were introduced. The research direction of hot-dip galvanized rebar was pointed out.
参考文献
| [1] | 孙成,李洪锡,张淑泉,高立群,黄磊,周晓晔.钢筋混凝土腐蚀研究综述[J].材料导报,2000(05):27-28,73. |
| [2] | 钟亚伟,李固华.沿海混凝土耐久性研究综述[J].四川建筑科学研究,2007(01):90-95. |
| [3] | 高明赞,徐天宁,蒋海平,干伟忠.混凝土结构外露金属耐久性研究进展[J].宁波工程学院学报,2007(04):42-46. |
| [4] | Ghosh R;Singh DDN .Kinetics, mechanism and characterisation of passive film formed on hot dip galvanized coating exposed in simulated concrete pore solution[J].Surface & Coatings Technology,2007(16/17):7346-7359. |
| [5] | 龚利华,诸伶俐.不锈钢在模拟混凝土孔隙液中的腐蚀行为研究[J].腐蚀科学与防护技术,2007(06):397-400. |
| [6] | M. Manna .Effect Of Steel Substrate For Phosphate Treatment: An Option To Simulate Tmt Rebar Surface[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(3):451-457. |
| [7] | Mohamed Al-Mehthel;Salah Al-Dulaijan;Saleh H. Al .Performance Of Generic And Proprietary Corrosion Inhibitors In Chloride-contaminated Silica Fume Cement Concrete[J].Construction and Building Materials,2009(5):1768-1774. |
| [8] | Ki Yong Ann;Ha-Won Song .Chloride threshold level for corrosion of steel in concrete[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(11):4113-4133. |
| [9] | SANCHEZ M;ALONSO M C;CECILIO P et al.Electrochemical and analytical assessment of galvanized steel reinforcement pre-treated with Ce and La salts under alkaline media[J].Cement and Concrete Composites,2006,28(03):256-266. |
| [10] | 杨建森,何党庆.钢筋混凝土中钢筋腐蚀的化学机理与防腐措施[J].宁夏大学学报(自然科学版),2001(03):298-301. |
| [11] | 曹楚南.悄悄进行的破坏--金属腐蚀[M].北京:清华大学出版社,2000:83-85. |
| [12] | LI M C;ROYER M;STIEN D et al.Inhibitive effect of sodium epcruate on zinc corrosion in alkaline solutions[J].Corrosion Science,2008,50(07):1975-1981. |
| [13] | Singh DDN;Ghosh R .Molybdenum-phosphorus compounds based passivator to control corrosion of hot dip galvanized coated rebars exposed in simulated concrete pore solution[J].Surface & Coatings Technology,2008(19):4687-4701. |
| [14] | Singh DDN;Yadav S .Role of tannic acid based rust converter on formation of passive film on zinc rich coating exposed in simulated concrete pore solution[J].Surface & Coatings Technology,2008(8):1526-1542. |
| [15] | 黄永昌,Ya Lipkin.55%Al-Zn-1.6%Si合金热浸镀工艺及耐蚀研究[J].腐蚀与防护,2000(06):266-268. |
| [16] | 李华飞,郑家燊,俞敦义.添加稀土对55%Al-Zn镀层的影响[J].华中科技大学学报(自然科学版),2003(05):107-109. |
| [17] | Shibli SMA;Jayalekshmi AC;Remya R .Electrochemical and structural characterization of the mixed oxides-reinforced hot-dip zinc coating[J].Surface & Coatings Technology,2007(16/17):7560-7565. |
| [18] | 卢锦堂;许乔瑜;孔纲.热浸镀技术与应用口[M].北京:机械工业出版社,2006 |
| [19] | LANGILL T J;DUGAN B.Zinc Materials for Use in Concrete[A].Oxford:Elsevier,2004:100. |
| [20] | JONES G M;SANKS R L;TCHOBANOGLOUS G.Pumping Station Design[M].Oxford:Elsevier,2008:1-52. |
| [21] | NARAYAN SWAMY R.Design for Durability with Galvanized Reinforcement[A].Oxford:Elsevier,2004:45. |
| [22] | The Use Of Inorganic Conversion Coatings To Enhance the Corrosion Resistance Of Reinforcement And The Bond strength At The Rebar/concrete[J].Construction and Building Materials,2009(1):233-238. |
| [23] | Bilal S. Hamad;Ghaida' K. Jumaa .Bond strength of hot-dip galvanized hooked bars in high strength concrete structures[J].Construction and Building Materials,2008(10):2042-2052. |
| [24] | Bilal S. Hamad;Ghaida' K. Jumaa .Bond strength of hot-dip galvanized hooked bars in normal strength concrete structures[J].Construction and Building Materials,2008(6):1166-1177. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%